乾燥条件の下での複合材料Zn/ZnS被膜の摩擦挙動の研究

Research on tribological behaviors of composite Zn/ZnS coating under dry condition

著者 (7件)： KANG Jia-jie (School of Engineering and Technol., China Univ. of Geosciences, Beijing 100083, CHN) ,  KANG Jia-jie (National Key Lab for Remanufacturing, Acad. of Armored Forces Engineering, Beijing 100072, CHN) ,  WANG Cheng-biao (School of Engineering and Technol., China Univ. of Geosciences, Beijing 100083, CHN) ,  WANG Hai-dou (National Key Lab for Remanufacturing, Acad. of Armored Forces Engineering, Beijing 100072, CHN) ,  XU Bin-shi (National Key Lab for Remanufacturing, Acad. of Armored Forces Engineering, Beijing 100072, CHN) ,  LIU Jia-jun (Dep. of Mechanical Engineering, Tsinghua Univ., Beijing 100084, CHN) ,  LI Guo-lu (School of Materials Sci. and Engineering, Hebei Univ. of Technol., Tianjin 300130, CHN)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 258  号： 6  ページ： 1940-1943  発行年： 2012年01月01日 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： この論文では,新規の化合物技術と組み合わせた高速アーク溶射と低温イオン硫化による複合材料Zn/ZnS被膜の作製について報告した。走査電子顕微鏡(SEM)によって表面と断面のモルフォロジーを観察した。Zn/ZnS被膜に対するX線回折(XRD)パターンは被膜が主としてZnとZnSからなっていることを示している。ナノ硬度と弾性率をナノインデンテーション試験機によって測定した。摩擦挙動を乾燥条件の下でボール-オン-ディスク試験機によって調べた。それらの結果は複合材料Zn/ZnS被膜の摩擦係数と摩耗深さは低く,安定であり,それが乾燥条件の下で優れた摩擦低減及び摩耗防止特性を有することを示している。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *硫化亜鉛 ,  *亜鉛 ,  *中炭素鋼 ,  *アーク溶射 ,  被覆 ,  硫化 ,  複合材料 ,  X線回折 ,  ナノインデンテーション ,  *微小硬さ ,  弾性係数 ,  摩擦係数 ,  耐摩耗性 ,  固体潤滑剤 ,  *潤滑膜
準シソーラス用語： AISI1045

分類 (3件)： 溶射  (WC08030N) ,  固体の機械的性質一般  (BL01021C) ,  潤滑法  (QB02020D)

タイトルに関連する用語 (7件)： 複合材料 ,  Zn ,  ZnS ,  被膜 ,  摩擦 ,  挙動 ,  研究