フロンタル重合により調製したポリ(N-ビニルカプロラクタム)のグラフェン-含有熱応答性ナノ複合材料ヒドロゲルの合成およびキャラクタリゼーション

Synthesis and Characterization of Graphene-Containing Thermoresponsive Nanocomposite Hydrogels of poly(N-Vinylcaprolactam) Prepared by Frontal Polymerization

著者 (10件)： SANNA Roberta (Universita di Sassari, Sassari, ITA) ,  SANNA Davide (Universita di Sassari, Sassari, ITA) ,  ALZARI Valeria (Universita di Sassari, Sassari, ITA) ,  NUVOLI Daniele (Universita di Sassari, Sassari, ITA) ,  SCOGNAMILLO Sergio (Universita di Sassari, Sassari, ITA) ,  PICCININI Massimo (Porto Conte Ricerche S.r.l., Sassari, ITA) ,  LAZZARI Massimo (Univ. Santiago de Compostela, Santiago de Compostela, ESP) ,  GIOFFREDI Emilia (Politecnico di Torino, Alessandria, ITA) ,  MALUCELLI Giulio (Politecnico di Torino, Alessandria, ITA) ,  MARIANI Alberto (Universita di Sassari, Sassari, ITA)
資料名： Journal of Polymer Science. Part A. Polymer Chemistry  (Journal of Polymer Science. Part A. Polymer Chemistry)
巻： 50  号： 19  ページ： 4110-4118  発行年： 2012年10月01日 
JST資料番号： C0337C  ISSN： 0887-624X  CODEN： JPLCAT  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： グラフェンを含む熱応答性ポリ(N-ビニルカプロラクタム)ナノ複合材料ヒドロゲルをフロンタル重合により合成できた。液体単量体中でグラファイトを直接超音波処理することにより,高濃度のグラフェンを得た。このようにどんな化学操作も必要とせずに一般的な酸化誘導体に替わるナノ充填剤して,”本物”のグラフェンを得ることができた。これらの単量体/グラフェンマスタバッチ分散系に架橋剤(テトラエチレングリコールジアクリラート)および開始剤(トリヘキシルテトラデシルホスホニウムペルオキソ硫酸塩)を添加し,重合した。結果から,最終的に除去する溶媒を用いずに対応するナノ複合材料を生成できた。材料をRaman,SEMおよびTEM観察により特性解析し,膨潤挙動およびレオロジー特性も研究した。

シソーラス用語： ラジカル重合 ,  *炭素材 ,  *ナノ複合材料 ,  *ヒドロゲル ,  機能性高分子 ,  架橋剤 ,  架橋重合 ,  重合体 ,  グラファイト ,  熱応答 ,  重合開始剤 ,  ホスホニウム ,  ペルオキソ硫酸塩 ,  膨潤 ,  レオロジー ,  温度依存性 ,  ラクタム ,  *グラフェン
準シソーラス用語： フロンタル重合 ,  熱応答性高分子

分類 (2件)： 物理的性質一般  (YH02021U) ,  単独重合  (CG04020S)

物質索引 (2件)： N-ビニルカプロラクタム ,  テトラエチレングリコールジアクリラート

タイトルに関連する用語 (8件)： フロンタル重合 ,  調製 ,  N-ビニルカプロラクタム ,  グラフェン ,  熱応答性 ,  ナノ複合材料 ,  ヒドロゲル ,  キャラクタリゼーション