直接分散エレクトロスピニングによる高固形分Co_0.8Ni_0.2Fe₂O₄/PVP複合ナノファイバーの作製とキャラクタリゼーション

Fabrication and characterization of high solid content Co_0.8Ni_0.2Fe₂O₄/PVP composite nanofibers by direct-dispersed electrospinning

著者 (6件)： TANG Ya (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Donghua Univ., Shanghai 201620, CHN) ,  TANG Ya (Coll. of Materials Sci. and Engineering, Donghua Univ., Shanghai 201620, CHN) ,  WANG Xinwei (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Donghua Univ., Shanghai 201620, CHN) ,  ZHANG Qinghong (Coll. of Materials Sci. and Engineering, Donghua Univ., Shanghai 201620, CHN) ,  LI Yaogang (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Donghua Univ., Shanghai 201620, CHN) ,  WANG Hongzhi (Coll. of Materials Sci. and Engineering, Donghua Univ., Shanghai 201620, CHN)
資料名： Synthetic Metals  (Synthetic Metals)
巻： 162  号： 3-4  ページ： 309-313  発行年： 2012年03月 
JST資料番号： C0123B  ISSN： 0379-6779  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高いCo_0.8Ni_0.2Fe₂O₄ナノ粒子含有量の複合ナノファイバーを,エレクトロスピニングにより作製した。シランカップリング剤改質磁性ナノ粒子を,直接3:1の質量比でポリビニルピロリドン(PVP)溶液に分散させた。得られたナノファイバーの表面モルフォロジーおよび構造を,電界放射走査型電子顕微鏡(FESEM),透過型電子顕微鏡(TEM)および振動試料型磁気測定計(VSM)によってキャラクタリゼーションした。FESEM,TEM観察の結果は,複合ナノ繊維の平均直径は350±30nmであり,改質磁性ナノ粒子は均一にポリマーマトリックス中に分散されていることが明らかになった。VSMの結果は,複合ナノファイバーの飽和磁化は最大29.8emu/gであり,またこの繊維が超常磁性挙動であることを示した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *エレクトロスピニング ,  *ポリビニルピロリドン ,  *ナノファイバ ,  *ナノ複合材料 ,  *高分子有機-無機ハイブリッド ,  *酸化鉄 ,  ナノ粒子 ,  コバルト化合物 ,  ニッケル化合物 ,  ニッケルフェライト ,  超常磁性 ,  飽和磁化 ,  走査電子顕微鏡 ,  電界放出 ,  複合繊維 ,  磁力計 ,  *有機磁性体
準シソーラス用語： *PVP【ポリマ】 ,  電界放射走査電子顕微鏡 ,  振動試料型磁力計

分類 (1件)： 高分子固体の物理的性質  (CG02024U)

物質索引 (1件)： 3-メルカプトプロピルトリメトキシシラン

タイトルに関連する用語 (6件)： エレクトロスピニング ,  固形分 ,  PVP ,  ナノファイバー ,  作製 ,  キャラクタリゼーション