マグネシア透過性多孔質パージプラグの高温曲げ強さに関する研究

Study on High Temperature Bending Strength of Magnesia Permeable Porous Purging Plug

著者 (6件)： You Jiegang (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...) ,  Zhang Guodong (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...) ,  Zhang Ling (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...) ,  Chen Ying (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...) ,  Zheng Yu (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...) ,  Jiang Chuang (The Magnesia Materials Engineering Res. Center Liaoning,High-temperature Materials and Magnesia Resources ...)
資料名： Guisuanyan Tongbao  (Guisuanyan Tongbao)
巻： 31  号： 1  ページ： 140-144  発行年： 2012年 
JST資料番号： C2439A  ISSN： 1001-1625  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： タンディッシュマグネシアの分散多孔質プラグの高温曲げ強さに及ぼす融解マグネシア(0.2~0mm)(質量比率,0%,3%,6%),α-Al_2O_3粉末(0.044mm,質量比率,5%,8%,10%),融解マグネシア粉末(0.044mm,質量比率,0,2%,3%)およびCr_2O_3粉末(0.044mm)(質量比率,0,2%,3%)によってブレンドされた添加剤の含有量の影響を4つのカラムと3本のラインを用いて直角配列によって研究した。この結果は,マグネシア分散多孔質プラグに及ぼす融解マグネシア(0.2~0mm)影響が最も先であり,次にCr_2O_3粉末,融解マグネシア粉末およびα-Al_2O_3粉末であることを示した。マグネシア分散多孔質プラグの高温曲げ強さに及ぼす融解マグネシアとCr_2O_3粉末の影響は目に見えるものであり,融解マグネシア粉末はこのマグネシア分散多孔質プラグの高温曲げ強さに影響を与えた。α-Al_2O_3粉末の影響は明らかではなかった。最良処方はA3B2C2D2であった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *酸化マグネシウム ,  多孔性 ,  *曲げ強さ ,  高温 ,  *プラグ ,  タンディッシュ ,  融解 ,  粉体
準シソーラス用語： *マグネシア ,  多孔質 ,  粉末