Mg-Al-Ce-Y系高圧ダイカスト合金の構造安定性と機械的性質

Structure stability and mechanical properties of high-pressure die-cast Mg-Al-Ce-Y-based alloy

著者 (6件)： Zhang Jinghuai (Harbin Engineering Univ. Key Lab. of Superlight Materials & Surface Technol. of Ministry of Education, Harbin) ,  Liu Shujuan (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Leng Zhe (Harbin Engineering Univ. Key Lab. of Superlight Materials & Surface Technol. of Ministry of Education, Harbin) ,  Zhang Milin (Harbin Engineering Univ. Key Lab. of Superlight Materials & Surface Technol. of Ministry of Education, Harbin) ,  Meng Jian (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Rare Earth Resources Utilization ...) ,  Wu Ruizhi (Harbin Engineering Univ. Key Lab. of Superlight Materials & Surface Technol. of Ministry of Education, Harbin)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 22  号： 2  ページ： 262-267  発行年： 2012年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： Mg-Al-RE系合金の機械的性質を向上させるために,Mg-3.0Al-1.8Ce-0.3Y-0.2Mn合金を高圧ダイカスト法で製造した。微細構造,中間相の熱安定性,および機械的性質を研究した。試験結果から,合金は,微細な初析α-Mgデンドライトとデンドライト間領域の共晶から成ることがわかった。共晶の中間相は,Al_(11)(Ce,Y)_3とAl_2(Ce,Y)であり,前者が優勢なものであった。Al_(11)(Ce,Y)_3の熱安定性は制約された。800時間以内では,それは基本的に200°Cまで安定であるが,大部分のAl_(11)(Ce,Y)_3金属間化合物は,より高い温度の450°Cにおいて800時間でAl_2(Ce,Y)に変換した。室温と200°Cの両方で,合金は大幅に向上した強度を示した。それは,主にAl_(11)(Ce,Y)_3金属間化合物でのデンドライト境界の強化,狭いデンドライトアーム間隔の効果,およびY元素での固溶体強化のせいであった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *安定性 ,  機械的性質 ,  アルミニウム ,  セリウム ,  マグネシウム ,  ダイカスト ,  金属間化合物 ,  微細構造 ,  熱安定性 ,  マンガン合金
準シソーラス用語： *構造安定性 ,  Al ,  Ce ,  Mg ,  高圧ダイカスト ,  ダイカスト法 ,  Mn合金