寸法の異なる円錐形ダイを用いて調製した超高分子量ポリエチレン繊維

Ultrahigh Molecular Weight Polyethylene Fibers Prepared Using Conical Dies With Varying Dimensions

著者 (14件)： YEH Jen-Taut (National Taiwan Univ. Sci. and Technol., Taipei, TWN) ,  YEH Jen-Taut (Wuhan Univ. Sci. and Engineering, Wuhan, CHN) ,  YEH Jen-Taut (Hubei Univ., Wuhan, CHN) ,  YEH Jen-Taut (Kun Shan Univ., Tainan) ,  YEH Jen-Taut (Wuhan Univ., Wuhan, CHN) ,  WANG Chuen-Kai (National Taiwan Univ. Sci. and Technol., Taipei, TWN) ,  ZHOU Qin (Wuhan Univ. Sci. and Engineering, Wuhan, CHN) ,  ZHOU Huo-Peng (Wuhan Univ. Sci. and Engineering, Wuhan, CHN) ,  TSAI Chih-Chen (National Taiwan Univ. Sci. and Technol., Taipei, TWN) ,  LAI Yu-Ching (National Taiwan Univ. Sci. and Technol., Taipei, TWN) ,  TSOU Chi-Hui (National Taiwan Univ. Sci. and Technol., Taipei, TWN) ,  CHEN Kan-Nan (Tamkang Univ., New Taipei City, TWN) ,  HUANG Chi-Yuan (Tatung Univ., Taipei, TWN) ,  LEE Kuei-Chi (Chinese Culture Univ., Taipei, TWN)
資料名： Polymer Engineering & Science  (Polymer Engineering & Science)
巻： 53  号： 9  ページ： 1910-1919  発行年： 2013年09月 
JST資料番号： C0640A  ISSN： 0032-3888  CODEN： PYESA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 超高分子量ポリエチレン(UHMWPE)ゲルを円錐形ノズルから大きい延伸比(Dra)(10-19)で延伸紡糸することによって高張力糸が得られることが報告されている。この場合ゲル組成,温度その他の因子が最大延伸比に影響する。これは分子の絡み合いと関係がある。本報においてはノズル形状(導入部円錐角,ノズル長,ノズル径)を変えて紡糸し,得られたフィラメントの特性(DSC測定による熱特性,動的機械特性)及びそれを延伸したフィラメントの特性(最大延伸比,表面形状,配向度,動的機械特性)を調べた。最高の配向度と延伸比は導入部円錐角75°,ノズル長6.5mm及び原液濃度20%において得られた。

シソーラス用語： *超高分子量ポリエチレン ,  *溶融紡糸 ,  *フィラメント糸 ,  *繊維特性 ,  *紡糸口金 ,  依存性 ,  比率 ,  ゲル ,  濃度依存性 ,  角度 ,  形態 ,  長さ ,  直径 ,  示差走査熱量測定 ,  動的機械分析 ,  機械的性質 ,  *熱特性 ,  *分子配向 ,  最適条件
準シソーラス用語： *形状依存性 ,  *延伸比 ,  高分子ゲル ,  円錐角 ,  ノズル形状 ,  DSC測定 ,  *動的機械特性 ,  表面形状 ,  配向【分子】

分類 (4件)： ポリオレフィン  (YH07090L) ,  半合成・合成繊維  (YM03030K) ,  高分子溶液・融液のレオロジー  (BL01013Z) ,  繊維物理  (YM02020S)

タイトルに関連する用語 (5件)： 円錐形 ,  ダイ ,  調製 ,  高分子量 ,  ポリエチレン繊維