グラフェン-銀ナノ粒子複合材料の製造とキャラクタリゼーション

Fabrication and Characterization of Graphene-Ag Nanoparticles Composites

著者 (6件)： Yu Mei (Key Lab. of Aerospace Materials and Performance,Ministry of Education,School of Materials Sci. and ...) ,  Liu Pengrui (Key Lab. of Aerospace Materials and Performance,Ministry of Education,School of Materials Sci. and ...) ,  Sun Yujing (State Intellectual Property Office of the People’s Republic of China, Beijing) ,  Liu Jianhua (Key Lab. of Aerospace Materials and Performance,Ministry of Education,School of Materials Sci. and ...) ,  An Junwei (Key Lab. of Aerospace Materials and Performance,Ministry of Education,School of Materials Sci. and ...) ,  Li Songmei (Key Lab. of Aerospace Materials and Performance,Ministry of Education,School of Materials Sci. and ...)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 27  号： 1  ページ： 89-94  発行年： 2012年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 還元剤として無毒のグリーンなグルコースを使用して,グラフェン-Agナノ粒子複合材料をワンステップin situ合成法によって調製した。酸化グラファイトとアンモニア性銀イオンを同時に安定剤なしで水溶液の穏和な反応条件の下で還元した。X線回折(XRD),Fourier変換赤外分光法(FT-IR),Ramanスペクトロスコープ,走査電子顕微鏡(SEM),および透過型電子顕微鏡(TEM)を用いて,得られた複合材料を特性評価した。分析の結果は,グラファイト酸化物とアンモニア性銀イオンがグルコースによって同時に還元されることを示した。Agナノ粒子(AgNPs)はグラフェンシート中に一様に分布して,AgNPsの大部分は双晶境界を示す。硝酸銀の量はAgNPsのサイズとサイジング範囲に影響する。グラフェンシート上のAgNPsのサイジングの範囲は,銀イオンの好適な濃度の下で,25nmに集中化する。複合材料中のグラフェンのRaman信号の強度は担持AgNPsによって7倍に増加する。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *炭素材 ,  *ナノ粒子 ,  *複合材料 ,  キャラクタリゼーション ,  化学合成 ,  グラファイト ,  酸化物 ,  金属イオン ,  銀化合物 ,  ヘキソース ,  アルドース ,  *グラフェン
準シソーラス用語： *銀ナノ粒子 ,  in situ合成 ,  酸化グラファイト ,  銀イオン

分類 (1件)： 化学工業一般  (YA01010Q)

物質索引 (1件)： グルコース

タイトルに関連する用語 (4件)： グラフェン ,  銀ナノ粒子 ,  複合材料 ,  キャラクタリゼーション