長期にわたる金属酸化障壁としてのグラフェン: 何もないよりもなお悪い

Graphene as a Long-Term Metal Oxidation Barrier: Worse Than Nothing

著者 (12件)： SCHRIVER Maria (Univ. California at Berkeley, California, USA) ,  SCHRIVER Maria (Lawrence Berkeley National Lab., California, USA) ,  REGAN William (Univ. California at Berkeley, California, USA) ,  REGAN William (Lawrence Berkeley National Lab., California, USA) ,  GANNETT Will J. (Univ. California at Berkeley, California, USA) ,  GANNETT Will J. (Lawrence Berkeley National Lab., California, USA) ,  ZANIEWSKI Anna M. (Univ. California at Berkeley, California, USA) ,  ZANIEWSKI Anna M. (Lawrence Berkeley National Lab., California, USA) ,  CROMMIE Michael F. (Univ. California at Berkeley, California, USA) ,  CROMMIE Michael F. (Lawrence Berkeley National Lab., California, USA) ,  ZETTL Alex (Univ. California at Berkeley, California, USA) ,  ZETTL Alex (Lawrence Berkeley National Lab., California, USA)
資料名： ACS Nano  (ACS Nano)
巻： 7  号： 7  ページ： 5763-5768  発行年： 2013年07月 
JST資料番号： W2326A  ISSN： 1936-0851  CODEN： ANCAC3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： グラフェンはガス透過性が低く,耐酸化性が良好であることから,新しいコーティング材料として期待が持たれている。本研究では,銅箔にグラフェン皮膜を化学蒸着し,FeCl₃水溶液を用いて銅の酸化及び腐食に対するグラフェン皮膜の効果を調べた。また,グラフェン皮膜をSiウエハ状に形成させ,同様に耐酸化性と耐食性を調べた。グラフェンの耐酸化及び耐食効果は,数分から数時間の時間スケールでは有効であった。しかし,それ以上の長い時間スケールでは何も被覆しない場合よりも著しく腐食が進行した。これは,グラフェン皮膜の欠陥部を通じて酸素及び水が浸透し,しかもグラフェンが腐食進行の触媒として働くためである。また,グラフェンは電気伝導性を有することから,電気化学的な腐食も併発する。本研究の結果は,グラフェンの応用に際して考慮すべき事項を提示するものである。

シソーラス用語： *耐食性 ,  *金属酸化物 ,  *炭素材 ,  透気性 ,  化学蒸着 ,  銅 ,  腐食 ,  耐酸化性 ,  導電性 ,  被覆 ,  *障壁 ,  X線光電子スペクトル ,  *銅箔 ,  塩化鉄 ,  ウエハ【IC】 ,  銅触媒 ,  被覆材 ,  *グラフェン
準シソーラス用語： Siウエハ

分類 (2件)： その他の無機化合物の薄膜  (BK14060A) ,  炭素とその化合物  (YB02060D)

タイトルに関連する用語 (4件)： 長期 ,  酸化 ,  障壁 ,  グラフェン