低温同時焼成NiCuZnフェライトの微細構造と磁気特性に及ぼすホウケイ酸ガラス添加の影響

Effects of borosilicate glass additions on microstructures and magnetic properties of low temperature co-fired NiCuZn ferrites

著者 (5件)： SHEN Wei (Nanjing Univ. of Technol., Coll. of Materials Sci. and Engineering, 210009, Nanjing, People’s Republic of China) ,  ZHU Haikui (Nanjing Univ. of Technol., Coll. of Materials Sci. and Engineering, 210009, Nanjing, People’s Republic of China) ,  ZHOU Hongqing (Nanjing Univ. of Technol., Coll. of Materials Sci. and Engineering, 210009, Nanjing, People’s Republic of China) ,  XU Zhiming (Jiangsu Huaxing Electronic Co., Ltd., 213234, Changzhou, People’s Republic of China) ,  JIN Yu (Nanjing Univ. of Technol., Coll. of Materials Sci. and Engineering, 210009, Nanjing, People’s Republic of China)
資料名： Journal of Materials Science. Materials in Electronics  (Journal of Materials Science. Materials in Electronics)
巻： 24  号： 12  ページ： 4713-4717  発行年： 2013年12月 
JST資料番号： W0003A  ISSN： 0957-4522  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 固相反応を用い,様々なホウケイ酸ガラス添加量の低温同時焼成NiCuZnフェライトを製造した。ホウケイ酸ガラス添加は,液相焼結と粒成長促進によって試料の緻密化を強化できた。少量のホウケイ酸ガラス添加は主相の形成に有意には影響しなかったが,多すぎる添加は磁気特性を損ねた。添加量を0~0.1wt%に増すと100kHzにおける透磁率は664から555に低下し,添加量を0.3~0.9wt%に増すと透磁率は310から169に低下した。0.1wt%添加量は抵抗率を4.07×10¹⁰Ωcmから9.81×10¹⁰Ωcmに増したが,0.9wt%添加量は不均一で粒内細孔を有する粒子を形成し,抵抗率を1.4×10¹⁰Ωcm迄低下させただけであった。Copyright 2013 Springer Science+Business Media New York Translated from English into Japanese by JST.

シソーラス用語： 固相反応 ,  *ホウケイ酸ガラス ,  *添加物効果 ,  依存性 ,  緻密化 ,  *微細構造 ,  *磁気的性質 ,  焼成 ,  透磁率 ,  電気抵抗率 ,  *フェライト ,  ニッケル化合物 ,  銅化合物 ,  亜鉛化合物 ,  磁性材料 ,  X線回折分析 ,  電子顕微鏡観察 ,  Q値
準シソーラス用語： 磁気特性 ,  走査電子顕微鏡観察 ,  低温焼成 ,  添加量依存性