方向性凝固したNiAl-31Cr-2.9Mo-0.1Hf-0.05Ho共晶合金の高温酸化挙動

High temperature oxidation behavior of directionally solidified NiAl-31Cr-2.9Mo-0.1Hf-0.05Ho eutectic alloy

著者 (7件)： Wang Zhensheng (Coll. of Electromechanical Engineering,Hunan Univ. of Sci. and Technol., Xiangtan) ,  Xie Yi (Inst. of Metal Res.,Chinese Acad. of Sciences, Shenyang) ,  Guo Jianting (Inst. of Metal Res.,Chinese Acad. of Sciences, Shenyang) ,  Zhou Lanzhang (Inst. of Metal Res.,Chinese Acad. of Sciences, Shenyang) ,  Hu Zhuangqi (Inst. of Metal Res.,Chinese Acad. of Sciences, Shenyang) ,  Zhang Guangye (Coll. of Electromechanical Engineering,Hunan Univ. of Sci. and Technol., Xiangtan) ,  Chen Zhigang (Coll. of Electromechanical Engineering,Hunan Univ. of Sci. and Technol., Xiangtan)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 22  号： 7  ページ： 1582-1587  発行年： 2012年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： NiAl-31Cr-2.9Mo-0.1Hf-0.05Hoの方向性凝固共晶合金の等温酸化挙動を走査電子顕微鏡観察とX線回折法を用いて研究した。試験結果から,900~1100°Cの温度域では,連続的Al_2O_3のスケールが形成され,耐酸化性は優れていることがわかった。温度が1150°Cまで上昇すると,連続的Al_2O_3酸化膜は破れた。合金中に均一分布した微量の希土類元素のホルミウムと,クロム(モリブデン)相中で相対的に高水準なアルミニウムは連続的で緻密なAl_2O_3スケールの形成に有利であった。酸化の際に,酸化膜の表面でθ-Al_2O_3からα-Al_2O_3への相変態が発生した。それは,合金を1000°Cか1050°Cで酸化したときに,異常な酸化質量増加の発生をもたらせた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 高温酸化 ,  *凝固 ,  共晶合金 ,  電子顕微鏡観察 ,  X線回折分析 ,  ホルミウム ,  モリブデン ,  希土類元素 ,  アルミニウム ,  酸化
準シソーラス用語： *方向性凝固 ,  走査電子顕微鏡観察 ,  X線回折法 ,  等温酸化