POE/EVA化合物発泡材の性質

Properties of the POE/EVA Compound Foaming Material

著者 (6件)： Chen Bo (The Inst. of Materials and Metallurgy of Guizhou Univ.,National Engineering Res. Center for Compounding and ...) ,  Lu Shengjun (The Inst. of Materials and Metallurgy of Guizhou Univ.,National Engineering Res. Center for Compounding and ...) ,  Yu Jie (National Engineering Res. Center for Compounding and Modification of Polymer Materials, Guizhou, Guiyang) ,  Gong Wei (Guizhou Province Materials Technol. Innovation Base,National Engineering Res. Center for Compounding and ...) ,  Guo Jianbing (National Engineering Res. Center for Compounding and Modification of Polymer Materials, Guizhou, Guiyang) ,  Zhang Chun (National Engineering Res. Center for Compounding and Modification of Polymer Materials, Guizhou, Guiyang)
資料名： Suliao  (Suliao)
巻： 41  号： 5  ページ： 52-55  発行年： 2012年 
JST資料番号： C2207A  ISSN： 1001-9456  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 基質としてポリエチレン-酢酸ビニル(EVA)を用いて,エチレン-オクテン共重合体(POE)の種々の含量と無水マレイン酸(MAH)グラフト化エチレン-オクテン共重合体(POE)複合発泡材を化学的発泡法で調製した。発泡挙動とEVA発泡材の機械特性に及ぼすPOEの影響を研究した。結果は,POE含量の増加で,発泡材の屈曲性は増加した,そして,圧縮率は減少したことを示した。しかし,引張と引裂き強さは減少した。他方では,セル直径は減少した,そして,セル密度は増加した,そして,POE含量が30%であったときに,最良性能セル直径は79.2μmであった。しかしながら,POE-g-MAH含量の増加で,フォーム引張,引裂き強さ,および耐摩耗性はかなり増加した。他方では,セル直径がさらに減少した,そして,セル密度は増加した。30%から40%の間の含量のとき,無水マレイン酸グラフト化POE発泡材の性能が最も良かった,そのセル直径は68.1μmであった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 共重合体 ,  ポリエチレン ,  化学修飾 ,  *材料 ,  起泡 ,  機械的性質 ,  屈曲度 ,  アルケン ,  脂肪酸 ,  脂肪族アルコール ,  エノールエステル ,  ビニル化合物 ,  不飽和アルコール ,  酸素複素環化合物 ,  脂肪族カルボン酸 ,  オレフィン化合物 ,  不飽和カルボン酸 ,  カルボン酸無水物 ,  ジカルボン酸 ,  グラフト化【化学修飾】
準シソーラス用語： オクテン ,  グラフト化 ,  *発泡材 ,  発泡 ,  機械特性 ,  屈曲性

分類 (1件)： 化学工業一般  (YA01010Q)

物質索引 (3件)： エチレン ,  酢酸ビニル ,  無水マレイン酸

タイトルに関連する用語 (4件)： POE ,  EVA ,  発泡材 ,  性質