ウシのリンパ液における窒素イオン・インプランテーションのための生体・医用Ti6Al7Nb合金の捩りフレッチング摩耗

Torsional fretting wear of a biomedical Ti6Al7Nb alloy for nitrogen ion implantation in bovine serum

著者 (6件)： CAI Zhen-bing (Tribology Res. Inst., Key Lab of Advanced Technologies of Materials (Ministry of Education), Southwest Jiaotong ...) ,  ZHANG Guang-an (State Key Lab. of Solid Lubrication, Lanzhou Inst. of Chemical Physics, Chinese Acad. of Sciences, Lanzhou 730000, CHN) ,  ZHU Yong-kui (Tribology Res. Inst., Key Lab of Advanced Technologies of Materials (Ministry of Education), Southwest Jiaotong ...) ,  SHEN Ming-xue (Tribology Res. Inst., Key Lab of Advanced Technologies of Materials (Ministry of Education), Southwest Jiaotong ...) ,  WANG Li-ping (State Key Lab. of Solid Lubrication, Lanzhou Inst. of Chemical Physics, Chinese Acad. of Sciences, Lanzhou 730000, CHN) ,  ZHU Min-hao (Tribology Res. Inst., Key Lab of Advanced Technologies of Materials (Ministry of Education), Southwest Jiaotong ...)
資料名： Tribology International  (Tribology International)
巻： 59  ページ： 312-320  発行年： 2013年03月 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Ti6Al7Nbは股関節置換など高い生体適合性を要求される外科インプラント用の高強度Ti合金である。窒素ガス処理(窒素のプラズマイオン埋込み堆積)されたこの合金を対象に,処理されたこの合金と直径25.2mmのZr₂O製の球との捩りフレッチング(TF)摩耗試験を,リンパ液の介在を模擬した環境条件下で計画実施した。摩擦の機械力学挙動解析,3D輪郭の観察,SEM形態学,表面成分分析の結果を基に,表面修飾層とその基盤層の損傷特性と,損傷への窒素イオン密度と捩り角変位振幅の影響を調べた。結果は,イオン堆積成層はTF摩耗への抵抗性を改善可能で人工インプラントのTF損傷予防に使える可能性あり,を示した。この合金でのイオン埋込み層により予防される損傷メカニズムは,酸化摩耗と剥離・アブレシブ摩耗の双方で,イオン埋込み濃度の増加は剥離による離脱を予防する。Copyright 2013 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *チタン合金 ,  *滑り摩耗 ,  損傷 ,  ねじり変形 ,  イオン窒化 ,  イオン注入 ,  *医用素材 ,  *摩耗特性 ,  摩耗試験 ,  表面改質 ,  リンパ
準シソーラス用語： フレッチング ,  フレッチング摩耗

分類 (3件)： 医用素材  (GA05040H) ,  金属の機械的性質  (BL01022T) ,  潤滑一般  (QB02010S)

タイトルに関連する用語 (7件)： ウシ ,  リンパ液 ,  窒素イオン ,  インプランテーション ,  生体 ,  捩り ,  フレッチング摩耗