Al-Cu-Mg-Ag合金の時効挙動のシンクロトロン放射小角度X線散乱調査

Small-angle X-ray scattering investigation of aging behavior of Al-Cu-Mg-Ag alloys using synchrotron radiation

著者 (6件)： Zhang Jianbo (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing) ,  Zhang Yongan (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing) ,  Zhu Baohong (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing) ,  Liu Ruiqing (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing) ,  Li Zhihui (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing) ,  Li Xiwu (General Res. Inst. for Nonferrous Metals State Key Lab. of Nonferrous Metals and Processes, Beijing)
資料名： Rare Metals  (Rare Metals)
巻： 31  号： 6  ページ： 537-540  発行年： 2012年 
JST資料番号： C2573A  ISSN： 1001-0521  CODEN： RARME8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 高いCu/Mgを含有するAl-Cu-Mg-Ag合金の時効挙動を,透過型電子顕微鏡(TEM)およびシンクロトロン放射小角度X線散乱(SAXS)によって研究した。TEM研究により,10時間160°Cの時効後の合金の主要強化相は,Ωおよび小量のθ’であった。SAXS研究により,散乱パターンは,時効過程の初めに,いくつかの同心円から成り,そしてそれは,時効時間の増加とともに,蝶羽根状散乱パターンによって置き換えられた。蝶羽根状散乱パターンは,いくつかの分岐から成った。分岐間の角度は,析出物の癖面間の角度に,おおよそ等しかった。時効時間増加によるGuinier半径の増加は,析出物の良好な結晶粒粗大化抵抗を示した。積分強度の増加は,古典的2段階析出過程と一致した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *合金 ,  *時効 ,  シンクロトロン放射 ,  小角X線散乱 ,  透過型電子顕微鏡 ,  析出物 ,  結晶粒粗大化