共析出レオロジ-位相法で調製された,YAG:Ce(3+)蛍光体の光蛍光強化

Photoluminescence enhancement of YAG:Ce(3+) phosphor prepared by co-precipitation-rheological phase method

著者 (6件)： Ye Xinyu (School of Metallurgy and Chemistry Engineering,Jiangxi Univ. of Sci. and Technol., Ganzhou) ,  Long Zhen (School of Materials Sci. and Engi-neering,Southwest Univ. of Sci. and Technol., Mianyang) ,  Yang Youming (School of Metallurgy and Chemistry Engineering,Jiangxi Univ. of Sci. and Technol., Ganzhou) ,  Nie Huaping (School of Metallurgy and Chemistry Engineering,Jiangxi Univ. of Sci. and Technol., Ganzhou) ,  Guo Yanwei (School of Metallurgy and Chemistry Engineering,Jiangxi Univ. of Sci. and Technol., Ganzhou) ,  Cai Yufa (School of Metallurgy and Chemistry Engineering,Jiangxi Univ. of Sci. and Technol., Ganzhou)
資料名： Journal of Rare Earths  (Journal of Rare Earths)
巻： 30  号： 1  ページ： 21-24  発行年： 2012年 
JST資料番号： W0092A  ISSN： 1002-0721  CODEN： JREAE6  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： ]YAG:Ce(3+)蛍光体を,新規共析出レオロジ-相法を用いて調製した。得られたYAG:Ce(3+)蛍光体は,X線回折(XRD),走査型電子顕微鏡観察(SEM)と光輝性発光スペクトルを用いて特性評価した。酢酸を溶媒として用いることにより,小粒子(≦2μm)YAG:Ce(3+)粉末を1400oCの比較的低い焼結温度で得た。酢酸量の増加により,小粒子は溶けて見えなくなった。しかしながら,より大きい粒子が部分的に成長し,球状から直角に形態変化した。一方,共析出レオロジ-相法で調製したサンプルの発光強度は,共析出方法で調製した試料より約43%高かった。ルミネセンスの有意な改善は,主としてレオロジ-相がより良い拡散環境を示し,それゆえ,Ce3+の活性化剤のより良い均質性によると推定した。Data from the ScienceChina, LCAS. Translated by JST