スルホン化ポリエーテルスルホン電解質膜の性能に及ぼす骨格剛性の影響

Influence of Backbone Rigidness on the Performance of Sulfonated Polyether Sulfone Electrolyte Membranes

著者 (7件)： Liu Jianmei (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Hu Zhaoxia (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Chen Shanshan (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Rong Yi (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Wang Mingdong (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Wei Songbo (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing) ,  Chen Shouwen (School of Environmental and Biological Engineering,Nanjing Univ. ofScience & Technol., Nanjing)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 28  号： 5  ページ： 85-88  発行年： 2012年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 一連の新規スルホン化ポリアリーレンエーテルスルホン(SPAES)共重合体を,6F-ビスフェノールA(HFBPA),9,9′-ビス(4-ヒドロキシフェニル)フッ素(BHPF),4,4′-ジフルオロジフェニルスルホン(DFDPS)および3,3′-ジスルホナート-4,4′-ジフルオロジフェニルスルホン(SDFDPS)の高温共重合により,首尾よく合成した。ポリマー骨格の剛性は,HFBPAに対するBHPFの比率で制御できた。BHPFの比率増加に伴い,SPAES膜は,水に対する安定性は向上するが,吸水率およびプロトン伝導性は低下した。SPAES50-50(BHPF/HFBPAのモル比50/50およびスルホン化度50%)の膜は,平面および厚み方向での寸法変化は,それぞれ,0.12および0.13であり,水中,60°Cでのプロトン伝導性が,0.137S/cmで,ならびに,水中130°C,200時間のエージング処理で,質量損失が7%であり,高温燃料電池分野でのそれらの有望な可能性を示唆した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *電解質 ,  *膜 ,  *剛性 ,  *ポリエーテルスルホン ,  共重合体 ,  共重合 ,  高温燃料電池 ,  重合体 ,  質量欠損 ,  モル比 ,  吸水率
準シソーラス用語： *スルホン化ポリエーテルスルホン ,  *電解質膜 ,  ポリマ ,  質量損失