Gold nanolayer and nanocluster coatings induced by heat treatment and evaporation technique

著者 (8件)： SCHAUB Anna (Inst. of Chemical Technol., Dep. of Solid State Engineering, 166 28, Prague, CZE) ,  SLEPICKA Petr (Inst. of Chemical Technol., Dep. of Solid State Engineering, 166 28, Prague, CZE) ,  KASPARKOVA Irena (Inst. of Chemical Technol., Dep. of Solid State Engineering, 166 28, Prague, CZE) ,  MALINSKY Petr (Acad. of Sciences of the Czech Republic, Nuclear Physics Inst., Rez, CZE) ,  MALINSKY Petr (J.E. Purkyne Univ., Fac. of Sci., Usti nad Labem, CZE) ,  MACKOVA Anna (Acad. of Sciences of the Czech Republic, Nuclear Physics Inst., Rez, CZE) ,  MACKOVA Anna (J.E. Purkyne Univ., Fac. of Sci., Usti nad Labem, CZE) ,  SVORCIK Vaclav (Inst. of Chemical Technol., Dep. of Solid State Engineering, 166 28, Prague, CZE)
資料名： Nanoscale Research Letters (Web)  (Nanoscale Research Letters (Web))
巻： 8  号： 1  ページ： 1-8  発行年： 2013年12月 
JST資料番号： U7001A  ISSN： 1931-7573  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,ガラス基板上へ蒸着した金の被覆とナノ構造の調製と特性評価に焦点を当てた。層を調製する様々な方法を適用した。金は(i)室温,(ii)300°Cへ加熱したガラス,そして(iii)室温で蒸着したガラス,その結果300°Cまでアニールされたガラス上に蒸着した。van der Pauw法により,シート抵抗と自由キャリア濃度を決定した。原子間力顕微鏡により表面形態を評価した。UV-vis分光法により,金ナノ構造の光学特性を測定した。蒸発法とガラスの同時加熱を組合せると,金ナノ構造のシート抵抗,表面粗さ,及び光学特性が変化した。蒸発過程の間基板を加熱すれば,著しく厚い膜厚(18nm)で電気的に連続な層が形成された。アニーリング過程は金ナノ構造の構造・光学特性が影響を受けた。蒸発中にガラスを高温にすると,この構造のプラズモン共鳴ピークが増幅され,表面形態は著しく変化する。Copyright 2013 Schaub et al.; licensee Springer. Translated from English into Japanese by JST.

シソーラス用語： *金 ,  基板 ,  蒸着膜 ,  *金属薄膜 ,  被覆層 ,  *シート抵抗 ,  *キャリア密度 ,  形態 ,  原子間力顕微鏡 ,  ナノ構造 ,  基板温度 ,  熱処理 ,  表面粗さ ,  *紫外可視吸収スペクトル ,  *ナノクラスタ
準シソーラス用語： ガラス基板 ,  表面形態

分類 (3件)： 金属薄膜  (BK14030T) ,  金属結晶の電子伝導  (BM03033M) ,  金属の可視・紫外スペクトル  (BM08082H)

タイトルに関連する用語 (6件)： 熱処理 ,  蒸発 ,  誘起 ,  金 ,  ナノ層 ,  ナノクラスタ