α-MnO2ナノロッドの水熱合成とそれらの電気化学性能

Hydrothermal Synthesis of α-MnO2 Nanorods and Their Electrochemical Performances

著者 (6件)： Xue Zhaohui (Key Lab. of Functional Inorganic Materials Chemistry of Ministry of Education, School of Chemistry and Materials ...) ,  Liu Zhaolin (Environment Protect Monitoring Center,Dalian Economic and Technical Dev. Zone, Liaoning, Dalian) ,  Ma Fangwei (Key Lab. of Functional Inorganic Materials Chemistry of Ministry of Education, School of Chemistry and Materials ...) ,  Sun Liping (Key Lab. of Functional Inorganic Materials Chemistry of Ministry of Education, School of Chemistry and Materials ...) ,  Huo Lihua (Key Lab. of Functional Inorganic Materials Chemistry of Ministry of Education, School of Chemistry and Materials ...) ,  Zhao Hui (Key Lab. of Functional Inorganic Materials Chemistry of Ministry of Education, School of Chemistry and Materials ...)
資料名： Wuji Huaxue Xuebao  (Wuji Huaxue Xuebao)
巻： 28  号： 4  ページ： 691-697  発行年： 2012年 
JST資料番号： C2431A  ISSN： 1001-4861  CODEN： WHUXEO  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： α-MnO2ナノロッドを120°C,3時間で過マンガン酸カリウム,GO(グラファイト酸化物)および硫酸の水熱処理によって調製した。このナノロッドは10~20nmの直径と300~400nmの長さを有した。GOの導入はナノロッドの調製温度を下げて,この反応時間を短くした。電気化学結果はα-MnO2ナノロッドが中性水成電解質(1mol L-1Na2SO4)中で微細容量性挙動を示すことを表して,このスキャン速度が2mV s-1と5mV s-1であるとき,この比静電容量はそれぞれ276F g-1と240F g-1であった。本α-MnO2ナノロッドは電気化学キャパシタにとっての可能性がある電極材料であった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *酸化マンガン ,  ナノロッド ,  水熱合成 ,  *電気化学 ,  カリウム化合物 ,  過マンガン酸塩 ,  グラファイト ,  酸化物 ,  硫酸
準シソーラス用語： 過マンガン酸カリウム ,  酸化グラファイト

分類 (2件)： 塩基,金属酸化物  (CD01030Z) ,  電気化学一般  (CB07010N)

タイトルに関連する用語 (4件)： MnO2 ,  ナノロッド ,  水熱合成 ,  電気化学