放電プラズマ焼結法によるW-30Re重合金のミクロ組織と特性に及ぼす焼結温度の影響

Effect of Sintering Temperature on Microstructure and Properties of W-30Re Heavy Alloy by Spark Plasma Sintering

著者 (6件)： Xie Ming (Kunming Univ. of Sci. and Technol., State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming) ,  Wang Song (State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming) ,  Zhang Jiming (State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming) ,  Yang Youcai (State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming) ,  Chen Yongtai (State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming) ,  Liu Manmen (State Key Lab. of Advanced Technologies for Comprehensive Utilization, Kunming)
資料名： Xiyou Jinshu Cailiao yu Gongcheng  (Xiyou Jinshu Cailiao yu Gongcheng)
巻： 41  号： 12  ページ： 2195-2198  発行年： 2012年 
JST資料番号： W0563A  ISSN： 1002-185X  CODEN： XJCGEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： W-30Re重合金を放電プラズマ焼結(SPS)法で製造した。合金の密度,硬さ,ミクロ組織,および破壊モードに及ぼす焼結温度の影響を研究した。試験結果から,SPS法で比較的短時間に微細結晶粒で均一ミクロ組織のW-30Re重合金を製造できることがわかった。焼結温度の上昇に伴い,焼結合金の密度と硬さは必ず増加し,合金中の結合相の数は増加した。合金の破壊モードは,典型的脆性粒界破壊から次第に劈開破壊と結合面の延性引裂き破壊に変わった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *放電焼結 ,  温度依存性 ,  金属組織 ,  加熱温度 ,  破壊モード ,  タングステン合金 ,  焼結合金 ,  テアリング破壊 ,  粒界破壊 ,  破壊 ,  微結晶 ,  *放電プラズマ焼結
準シソーラス用語： 温度効果 ,  ミクロ組織【金属組織】 ,  焼結温度 ,  重合金 ,  引裂き破壊 ,  劈開破壊 ,  微細結晶