430°Cの低温塩浴窒化浸炭化による2205二相ステンレス鋼の表面改質

Surface modification of 2205 duplex stainless steel by low temperature salt bath nitrocarburizing at 430°C

著者 (7件)： HUANG Runbo (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  WANG Jun (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  WANG Jun (State Key Lab of Oil and Gas Reservoir Geology and Exploitation, Southwest Petroleum Univ., Chengdu 610500, CHN) ,  ZHONG Si (Coll. of Life Sci. and Engineering, Southwest Jiaotong Univ., Chengdu 610031, CHN) ,  LI Mingxing (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  XIONG Ji (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  FAN Hongyuan (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 271  ページ： 93-97  発行年： 2013年04月15日 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 2205ステンレス鋼を430°Cの塩浴窒化浸炭によって改質した。微細構造や表面硬度および耐侵食-腐食性を系統的に評価した。430°Cの塩浴窒化浸炭は窒化浸炭層を形成し,処理時間が長くなると層の厚さが増加する。8h以内の窒化浸炭では膨張オーステナイト(S相)だけが形成された。処理時間を増すと,CrNが窒化浸炭前に層内のフェライト結晶粒が存在した場所から徐々に拡散した。さらに,深さは窒化浸炭時間と共に増加し,層は放物線速度則にほぼしたがって成長した。塩浴窒化浸炭は2205 DSSの表面硬度を効率的に改善できる。耐侵食-腐食性は塩浴窒化浸炭で改善され,16hの処理試料は最良の侵食-腐食挙動をもっている。Copyright 2013 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *二相鋼 ,  *ステンレス鋼 ,  塩浴 ,  *表面改質 ,  オーステナイト ,  微小硬さ ,  *耐食性 ,  *表面硬化 ,  *浸炭窒化
準シソーラス用語： *窒化浸炭 ,  膨張オーステナイト

分類 (2件)： 表面硬化熱処理  (WC03030E) ,  防食  (WB03040M)

タイトルに関連する用語 (5件)： 低温 ,  塩浴 ,  窒化浸炭 ,  二相ステンレス鋼 ,  表面改質