種々の基板上のエピタキシャルBa(Fe_1-xCo_x)₂As₂薄膜の構造及び輸送特性

Structural and transport properties of epitaxial Ba(Fe_1-xCo_x)₂As₂ thin films on various substrates

著者 (18件)： LEI Q Y (Temple Univ., Pennsylvani, USA) ,  GOLALIKHANI M (Temple Univ., Pennsylvani, USA) ,  YANG D Y (Temple Univ., Pennsylvani, USA) ,  WITHANAGE W K (Temple Univ., Pennsylvani, USA) ,  RAFTI A (Temple Univ., Pennsylvani, USA) ,  QIU J (Temple Univ., Pennsylvani, USA) ,  HAMBE M (Temple Univ., Pennsylvani, USA) ,  BAUER E D (Los Alamos National Lab., NM, USA) ,  RONNING F (Los Alamos National Lab., NM, USA) ,  JIA Q X (Los Alamos National Lab., NM, USA) ,  WEISS J D (Florida State Univ., F, USA) ,  HELLSTROM E E (Florida State Univ., F, USA) ,  WANG X F (Univ. science and Technol. of China, Anhui, CHN) ,  CHEN X H (Univ. science and Technol. of China, Anhui, CHN) ,  WILLIAMS F (Norfolk State Univ., VA, USA) ,  YANG Q (Norfolk State Univ., VA, USA) ,  TEMPLE D (Norfolk State Univ., VA, USA) ,  XI X X (Temple Univ., Pennsylvani, USA)
資料名： Superconductor Science and Technology  (Superconductor Science and Technology)
巻： 27  号： 11  ページ： 115010,1-9  発行年： 2014年11月 
JST資料番号： T0607A  ISSN： 0953-2048  CODEN： SUSTEF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 異なる基板(SrTiO₃,LaAlO₃,(La,Sr)(Al,Ta)O₃,MgO,CaF₂,BaF₂)の上にパルスレーザ蒸着によって適当にCoをドープしたBa(Fe_1-xCo_x)₂As₂薄膜を作製した。基板によって異なる格子定数の違いよって生じる格子歪の影響を調べた。そのためのX線回折測定および電気抵抗の温度依存性の測定を行った。その結果,圧縮歪がある膜は引張歪のある膜に比べて高い超伝導転移温度T_cを示すことが分かった。但し,エピタキシャル歪の符号と大きさは,膜と基板の格子不整合とは直接には関係しない。

シソーラス用語： *ヒ化物 ,  *鉄化合物 ,  *コバルト化合物 ,  *バリウム化合物 ,  *超伝導薄膜 ,  ドーピング ,  コバルト ,  基板 ,  チタン酸ストロンチウム ,  アルミン酸塩 ,  ランタン化合物 ,  ストロンチウム化合物 ,  酸化マグネシウム ,  フッ化カルシウム ,  フッ化バリウム ,  *X線回折 ,  *電気抵抗 ,  温度依存性 ,  *転移温度 ,  超伝導体 ,  格子不整合 ,  格子歪 ,  内部応力
準シソーラス用語： アルミン酸ランタン ,  *超伝導転移温度

分類 (2件)： その他の超伝導体の物性  (BM04025Q) ,  その他の無機化合物の結晶構造  (BK07030J)

タイトルに関連する用語 (4件)： エピタキシャル ,  Ba ,  薄膜 ,  輸送特性