上部吹き込み富化酸素による高リン鉄鉱石の溶融還元におけるリンの挙動

Behaviors of Phosphorus in Smelting Reduction of High-phosphorus Iron Ore by Top-blown Enriched Oxygen

著者 (5件)： Wei Ke (Engineering Res. Center of Metallurgical Energy Conservation and Emission Reduction, Ministry of Education, Fac. of ...) ,  Qing Shan (Engineering Res. Center of Metallurgical Energy Conservation and Emission Reduction, Ministry of Education, Fac. of ...) ,  Wang Hua (Engineering Res. Center of Metallurgical Energy Conservation and Emission Reduction, Ministry of Education, Fac. of ...) ,  Deng Wenlong (Engineering Res. Center of Metallurgical Energy Conservation and Emission Reduction, Ministry of Education, Fac. of ...) ,  Shi Zhe (Engineering Res. Center of Metallurgical Energy Conservation and Emission Reduction, Ministry of Education, Fac. of ...)
資料名： Guocheng Gongcheng Xuebao  (Guocheng Gongcheng Xuebao)
巻： 13  号： 1  ページ： 78-82  発行年： 2013年 
JST資料番号： W0401B  ISSN： 1009-606X  CODEN： CJPEB5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 酸素上部吹き込み溶融還元による高リン鉄鉱石の製鉄過程を研究し,そして,本過程におけるリン分布に及ぼすスラグ塩基度,酸素に対する炭素のモル比,製錬温度,酸素吹き込み時間(酸素純度99%)および酸素流量の影響を調査した。その結果,溶鉄中のリンは,温度の上昇とともに減少した。しかしながら,過度の温度は,復リン現象に導いた。一定範囲内のスラグ塩基度,酸素富化率および酸素適用時間の上昇とともに,脱りん速度は高められた。しかしながら,脱りん率は,酸素に対する炭素のモル比の上昇とともに低下した。最適条件は,温度1550°C,酸素に対する炭素のモル比1.0,スラグ塩基度1.1,酸素パージ時間10分,および酸素流量250L/hであった。これらの条件下で,溶鉄中のリン含有量は,0.068%であり,そして,脱りん率は,92%に達した。生成銑鉄を,製鋼に用いることができた。Data from the ScienceChina, LCAS. Translated by JST