Fe-0.2C-2Mn合金および関連した理論的解析におけるγ→α形質転換の動力学に関するホット変形の影響

EFFECT OF HOT DEFORMATION ON KINETICS OF γ→α TRANSFORMATION IN A Fe-0.2C-2Mn ALLOY AND RELATED THEORETICAL ANALYSES

著者 (5件)： Xia Yuan (Key Lab. of Advanced Materials of Ministry of Education,Dep. of Materials Sci. and Engineering, Tsinghua Univ., Beijing) ,  Yang Zhigang (Key Lab. of Advanced Materials of Ministry of Education,Dep. of Materials Sci. and Engineering, Tsinghua Univ., Beijing) ,  Li Zhaodong (Key Lab. of Advanced Materials of Ministry of Education,Dep. of Materials Sci. and Engineering, Tsinghua Univ., Beijing) ,  Zhang Yuduo (Key Lab. of Advanced Materials of Ministry of Education,Dep. of Materials Sci. and Engineering, Tsinghua Univ., Beijing) ,  Zhang Chi (Key Lab. of Advanced Materials of Ministry of Education,Dep. of Materials Sci. and Engineering, Tsinghua Univ., Beijing)
資料名： Jinshu Xuebao  (Jinshu Xuebao)
巻： 48  号： 3  ページ： 271-276  発行年： 2012年 
JST資料番号： B0626A  ISSN： 0412-1961  CODEN： CHSPA4  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： γ→α形質転換は,鉄鋼で最も一般で重要な反応の1つである。以前の実験的研究の多くは,ホット変形がフェライト粒子を精練することができて,低炭素合金鋼の強度およびじん性を非常に改良することができたことを,すでに明示した。関連した理論的研究以外の,特に定量的記述は,まだ深まりを必要とした。低炭素合金鋼における理論的基準を更に結晶粒微細化に提供する試みにおいて,研究対象としてFe-0.2C-2Mn合金を取り入れて,本研究は,両方の熱機械実験および理論的解析の方法によるオーステナイト→プロ-共析晶フェライト形質転換に関するホット変形の影響を調査した。OM観測は,歪の増加および変形温度とホット変形の縮小によって構成するより見事なフェライト粒子が,初析フェライトの形態を変えたことを示した。ピルボックスモデルおよび放物線状の成長モデルに基づいて,粒子限界核形成比率および放物線状の成長定数はホット変形状態に基づき個々に計算して,その両方は変形よって速めることを実証した。NPLEモードに基づき,フェライト核形成は拡散係数の増加および核形成サイトの量のために主に変形よって強化した,ところが,駆動力への保存した変形エネルギーの貢献はPLEモードに基づき要所役割を行った。比較はフェライト核形成に関する変形の補強影響と成長の間で製作して,核形成が大部分の温度範囲でより著しく速めたことを示した。このように,ホット変形の結晶粒微細化機構は,定量的に説明した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 合金 ,  *高温変形 ,  鉄鋼 ,  フェライト ,  低炭素合金鋼 ,  靱性 ,  結晶粒微細化 ,  オーステナイト ,  核形成 ,  拡散係数 ,  *相変態

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： Fe ,  理論 ,  解析 ,  形質転換 ,  動力学