加工熱処理の後のCu-Ni-Si-Zr合金の微細構造と特性

Microstructure and properties of Cu-Ni-Si-Zr alloy after thermomechanical treatments

著者 (6件)： Xiao Xiangpeng (General Res. Inst. for Nonferrous Metals State Key Lab. for Fabrication and Processing of Non-ferrous Metals, Beijing) ,  Xiong Baiqing (General Res. Inst. for Nonferrous Metals State Key Lab. for Fabrication and Processing of Non-ferrous Metals, Beijing) ,  Wang Qiangsong (General Res. Inst. for Nonferrous Metals State Key Lab. for Fabrication and Processing of Non-ferrous Metals, Beijing) ,  Xie Guoliang (General Res. Inst. for Nonferrous Metals State Key Lab. for Fabrication and Processing of Non-ferrous Metals, Beijing) ,  Peng Lijun (General Res. Inst. for Nonferrous Metals State Key Lab. for Fabrication and Processing of Non-ferrous Metals, Beijing) ,  Huang Guoxing (Aluminum Corp. of China Ltd. Luoyang Copper Co., Ltd., Luoyang)
資料名： Rare Metals  (Rare Metals)
巻： 32  号： 2  ページ： 144-149  発行年： 2013年 
JST資料番号： C2573A  ISSN： 1001-0521  CODEN： RARME8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： Cu-2.1Ni-0.5Si-0.2Zr合金の微細構造と特性に及ぼす加工熱処理の影響について調査した。熱間圧延板を1.5時間かけて920°Cで溶液処理して,水中で急冷して,厚さで70%減少まで冷間圧延して,次に数時間にわたって400,450および500°Cでエイジングした。この合金の引張強さと導電性における変動をエイジング時間の関数として評価した。この結果は450°C,2時間でエージングした合金に関して665MPaのピーク強度値を示した。しかし,導電性は450°C,8時間でエージングして47%のIACSの最高値に達することが観察された。OM,SEMおよびTEMをこの合金のミクロ構造検査のために用いた。析出は冷間圧延された合金中の変形帯域で優先的に発生した。特性挙動をミクロ構造特性の視点で考察した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 加工熱処理 ,  微細構造 ,  *合金 ,  時間 ,  強度 ,  引張強さ ,  処理 ,  冷間圧延 ,  熱間圧延 ,  導電性 ,  析出
準シソーラス用語： エイジング時間 ,  ピーク強度 ,  ミクロ構造 ,  溶液処理