High temperature tensile behaviors of twin-roll cast AZ31 Mg alloy

著者 (7件)： Qiao Jun (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  Bian Fubo (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  He Min (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  Zhang Qingfeng (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  Zhang Yongbin (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  Chen Min (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan) ,  Wang Yu (School of Materials Sci. and Metallurgy,Univ. of Sci. and Technol. Liaoning, Anshan)
資料名： Beijing Keji Daxue Xuebao  (Beijing Keji Daxue Xuebao)
巻： 35  号： 4  ページ： 503-509  発行年： 2013年 
JST資料番号： W1097A  ISSN： 1001-053X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 本論文は,ツイン-ロール鋳造AZ31マグネシウム合金のより高い温度引張変形反応および機構を報告した。300°Cから450°Cまで一定温度測距において,障害への伸びテストは,10(-3)s(-1)および10(-2)s(-1)の一定引張歪み比率に基づき実行した。そして,歪速度-変動引張テストは,2x10(-4)s(-1)から2x10(-2)s(-1)まで歪み比率に基づき実行した。引張比率が10(-2)s(-1)であるとき,400°Cおよび450°Cの材料の伸長は両方の100%を超えた。しかし,引張比率が10(-3)s(-1)であるとき,400°Cおよび450°Cの伸び価値は両方の200%を超えて,応力指数nはおよそ3であり,クリープ活性化エネルギーQは148.77kJ-mol(_1)であり,変形機構は粒界滑りおよび溶質-抗力崩壊クリープの協力的機構であった。光学顕微鏡法およびスキャン電子顕微鏡観察観測は,その動的再結晶および粒子成長のための障害端部の粗い粒子開発を示して,破砕は空洞成長および相関よって引き起こす引き延ばせるパターンであった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 鋳造 ,  *マグネシウム合金 ,  *引張 ,  温度 ,  歪 ,  応力指数 ,  クリープ ,  活性化エネルギー
準シソーラス用語： *AZ31マグネシウム合金 ,  引張歪

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： ロール ,  鋳造 ,  AZ31マグネシウム合金 ,  引張