文献

J-GLOBAL ID：201402274188387815   整理番号：13A1671067

ハロゲンフリーMPP難燃剤ポリプロピレン繊維の照射修飾

Irradiation modification of halogen-free MPP flame retardant polypropylene fibers

著者 (6件)： Cao Wenyue (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Jia Erpeng (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Yu Cihang (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Xu Jianjun (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Ye Guangdou (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Jiang Mengjin (State Key Lab. of Polymer Materials and Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu)
資料名： Hecheng Xianwei Gongye  (Hecheng Xianwei Gongye)
巻： 36  号： 1  ページ： 6-9  発行年： 2013年 
JST資料番号： C2123A  ISSN： 1001-0041  CODEN： HXIGEU  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ハロゲンフリー難燃剤ポリプロピレン(PP)繊維を,混合紡糸法により,自作のハロゲンフリー難燃剤(すなわち,ペンタエリスリトールスピロ環状リン酸塩(MPP)とPPのメラミン塩)から調製した。ハロゲンフリー抑制剤PP繊維を,低エネルギー電子照射によって修飾した。MPPの構造並びに繊維の機械的性質および難燃性を特性評価した。結果より,以下のことが分かった:自作のMPPは設計通りの構造を有していた;PP繊維の限界酸素指数(LOI)が上昇した;しかし,MPP含有量が増加している間,破断強さは低下した;MPPの質量分率を8%に制御したとき,繊維の破断強さは6.02CN/dtex,LOIは24.5%であった;質量分率で8%のMPPを含有する難燃性PP繊維のLOIは,低エネルギー電子照射線量の増加と共に上昇した;純粋なPP繊維のものと比較して,分解開始温度およびチャー残渣を,大きく増加し,燃焼後にチャー残渣の連続的かつコンパクトな構造が形成した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 難燃剤 ,  *ポリプロピレン繊維 ,  化学修飾 ,  照射 ,  紡糸 ,  機械的性質 ,  難燃性 ,  指数 ,  燃焼
準シソーラス用語： ハロゲンフリー ,  修飾【化学】 ,  限界酸素指数

分類 (1件)： 半合成・合成繊維  (YM03030K)

タイトルに関連する用語 (5件)： ハロゲン ,  MPP ,  難燃剤 ,  ポリプロピレン繊維 ,  修飾