J-GLOBAL ID：201402295600280637   整理番号：14A0016610

リチウムイオン電池用のLiVPO_4F/C基カソード材料の合成と性能

Synthesis and performance of LiVPO_4F/C-based cathode material for lithium ion battery

著者 (7件)： Wang Jiexi (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Wang Zhixing (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Shen Li (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Li Xinhai (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Guo Huajun (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Tang Weijia (School of Metallurgy and Environment, Central South Univ., Changsha) ,  Zhu Zhenguo (School of Metallurgy and Environment, Central South Univ., Changsha)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 23  号： 6  ページ： 1718-1722  発行年： 2013年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： LiVPO_4F/C基材料を前駆体加熱により調整し,H_2C_2O_42H_2O,NH_4H_2PO_4,NH_4VO_3およびLiFのスラリーのボールミル粉砕により得た。このプロセスにおいて,H_2C_2O_42H_2Oを還元剤と炭素源として用いた。前駆体と調整した試料の性質をTG-DTA,XRD,SEM,TEMおよびC-S分析によりキャラクタリゼーションした。XRD分析により,この前駆体が非晶質であり,調整したLiVPO_4F試料がLi_3V_2(PO_4)_3また少量のV_2O_3と共存していることを示した。平均粒度2μmの均一粉体をTEMにより観察した。HRTEM画像により,結晶粒子が非晶質炭素により均一に被覆され,その被覆層は約2nmであることを示した。合成した材料の比放電容量は0.1Cと10Cにおいてそれぞれ151.3と102.5mAh/gであり,電圧範囲は3.0-4.4V,および50サイクル後の10Cにおいて初期放電容量の90.4%を保持していた。LiVPO_4FとLi_3V_2(PO_4)_3に対応するV(3+)/V(4+)酸化還元ピークはCV曲線に近かった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *リチウムイオン電池 ,  *電極材料 ,  *リチウム含有合金 ,  バナジウム含有合金 ,  前駆体 ,  *ボールミル ,  還元剤 ,  X線回折 ,  走査電子顕微鏡 ,  透過型電子顕微鏡
準シソーラス用語： TG-DTA ,  *カソード材料 ,  ボールミル粉砕 ,  炭素源

分類 (3件)： 二次電池  (YB04030K) ,  粉砕,混合,造粒,乾燥  (YH04020R) ,  金属組織観察法  (WB01010R)

タイトルに関連する用語 (2件)： リチウムイオン電池 ,  カソード材料