A new 1.9GPa maraging stainless steel strengthened by multiple precipitating species

著者 (9件)： LI Yongcan (Inst. of Metal Res., Chinese Acad. of Sciences, Shenyang 110016, CHN) ,  LI Yongcan (Coll. of Materials Sci. and Technol., Nanjing Univ. of Aeronautics and Astronautics, Nanjing 210016, CHN) ,  YAN Wei (Inst. of Metal Res., Chinese Acad. of Sciences, Shenyang 110016, CHN) ,  COTTON James D. (The Boeing Co., 7755 East Marginal Way South, Seattle, WA 98108, USA) ,  RYAN Glamm J. (The Boeing Co., 7755 East Marginal Way South, Seattle, WA 98108, USA) ,  SHEN Yifu (Coll. of Materials Sci. and Technol., Nanjing Univ. of Aeronautics and Astronautics, Nanjing 210016, CHN) ,  WANG Wei (Inst. of Metal Res., Chinese Acad. of Sciences, Shenyang 110016, CHN) ,  SHAN Yiyin (Inst. of Metal Res., Chinese Acad. of Sciences, Shenyang 110016, CHN) ,  YANG Ke (Inst. of Metal Res., Chinese Acad. of Sciences, Shenyang 110016, CHN)
資料名： Materials & Design  (Materials & Design)
巻： 82  ページ： 56-63  発行年： 2015年10月05日 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 13Cr-13Co-4.5Ni-3.5Mo-0.5Ti(at%)の組成を有する新しい超高強度ステンレスマルエージング鋼を開発した。この鋼の破断引張り強さは,妥当な延性を備えて,1.9GPaに達する可能性があることが実証された。このブレークスルーは,三種類の異なる析出物による複合強化によって達成された。500°Cでの時効における析出物の大きさ,形態,化学組成の変化を,原子プローブ断層撮影法(APT)と透過型電子顕微鏡(TEM)を用いて調査した。析出物は,Ni-Ti-Alリッチクラスター,Moリッチクラスター,Crリッチクラスターの前駆体からそれぞれ成長した,η-Ni₃(Ti,Al)相,MoリッチR′相,Crリッチα′相であることを確認した。析出物/マトリックス界面においてMoとCr原子の偏析が検出され,η相の粗大化を抑制していると考えられた。観察結果に基づいて,これらの相の析出過程と機械的特性への影響を解析した。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *マルエージング鋼 ,  *ステンレス鋼 ,  *超強力鋼 ,  *時効処理 ,  *析出硬化 ,  *析出物 ,  相組成 ,  機械的性質 ,  引張強さ ,  降伏強さ ,  伸び率 ,  破壊靱性 ,  *トモグラフィー ,  化学組成 ,  サブゼロ処理
準シソーラス用語： *原子プローブトモグラフィー

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (2件)： 析出物 ,  強化