高結晶性球状h-BNの合成機構および合成プロセスの研究

The Research of the Synthesis Mechanism and Synthesis Process of High Crystallinity Globular h-BN

著者 (6件)： ZHANG Ning (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN) ,  ZHANG Tong (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN) ,  KAN Hongmin (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN) ,  WANG Xiaoyang (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN) ,  LONG Haibo (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN) ,  ZHOU Yonghui (Shenyang Univ., Liaoning Key Lab. of Advanced Materials Manufacturing Technol., 110044, Liaoning, CHN)
資料名： Journal of Inorganic and Organometallic Polymers and Materials  (Journal of Inorganic and Organometallic Polymers and Materials)
巻： 25  号： 6  ページ： 1495-1501  発行年： 2015年11月 
JST資料番号： W0462A  ISSN： 1574-1443  CODEN： JIOPE4  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本報ではポリマーネットワークを使用して異なる形態の六方晶窒化ホウ素(h-BN)を合成した。高結晶性球状h-BNの調製のために,ホウ酸(H₃BO₃)とホウ砂(Na₂B₄O₇10H₂O)混合部物をホウ素源として使用し,尿素(CO(NH₂)₂)を窒素源として使用した。実験は,合成機構と最適な合成プロセスを裏付けた。研究はh-BNの合成機構が,ホウ砂およびホウ酸が加熱され酸化ナトリウム(Na₂O)および酸化ホウ素(B₂O₃)へ分解することであるのを示した。流れるアンモニア(NH₃)雰囲気中で,B₂O₃は再びh-BNに転換された;合成温度の上昇と共にh-BNの結晶化度を徐々に増加した。高結晶性球状h-BNの最適合成温度は800°Cであった。黒鉛化指数は3.87で<5であり,h-BNは良い結晶化範囲内であった。Copyright 2015 Springer Science+Business Media New York Translated from English into Japanese by JST.

シソーラス用語： 硼砂 ,  *窒化ホウ素 ,  六方晶系 ,  前駆体 ,  ホウ酸 ,  アンモニア ,  結晶度 ,  黒鉛化 ,  アンモニウム化合物 ,  ペルオキソ硫酸塩 ,  化学合成 ,  熱分解 ,  架橋剤 ,  重合体 ,  ウレア化合物 ,  脂肪族カルボン酸 ,  カルボアミド ,  ビニル化合物 ,  不飽和カルボン酸
準シソーラス用語： *h-BN ,  過硫酸アンモニウム

分類 (1件)： 塩  (CD01050V)

物質索引 (3件)： 尿素 ,  N,N′-エチレンビスアクリルアミド ,  アクリルアミド

タイトルに関連する用語 (5件)： 高結晶性 ,  球状 ,  h-BN ,  プロセス ,  研究