改質で合成したalite-ye’elimiteセメントクリンカーの水和物特性

Hydration properties of the alite-ye’elimite cement clinker synthesized by reformation

著者 (5件)： LI Xuerun (State Key Lab. of Materials-Oriented Chemical Engineering, Coll. of Materials Sci. and Engineering, Nanjing Tech ...) ,  SHEN Xiaodong (State Key Lab. of Materials-Oriented Chemical Engineering, Coll. of Materials Sci. and Engineering, Nanjing Tech ...) ,  XU Jie (State Key Lab. of Materials-Oriented Chemical Engineering, Coll. of Materials Sci. and Engineering, Nanjing Tech ...) ,  LI Xiaodong (State Key Lab. of Materials-Oriented Chemical Engineering, Coll. of Materials Sci. and Engineering, Nanjing Tech ...) ,  MA Suhua (State Key Lab. of Materials-Oriented Chemical Engineering, Coll. of Materials Sci. and Engineering, Nanjing Tech ...)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 99  ページ： 254-259  発行年： 2015年11月30日 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 4.8%のye’elimiteを含有する膨張性早期高強度alite-ye’elimiteクリンカーを,原材料に鉱化剤を添加せず焼なまして合成した。ye’elimiteの改良は,クリンカー内でC$と反応するC₃Aで達成した。ペーストの微細構造は,SEM,MIPおよびN₂吸収/脱着によって特徴付けた。DSC-TGおよびXRDを用いて水和生成物を調査した。クリンカー試験による降伏値は,1,3および28日でそれぞれ30.0MPa,42.3MPaおよび55.8Mpaであった。水和したペースト内のAFtの存在により,膨張挙動は29-62%(0.01-10μm)の全細孔容積の減少の結果になった,しかしAFtの結晶により中細孔(2-50nm)がある。線形膨張は,最大膨張が150日以降で0.136%に収束した。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *セメント ,  *クリンカ ,  *水和物 ,  焼なまし ,  強度 ,  鉱化剤 ,  微細構造 ,  示差走査熱量測定 ,  X線回折 ,  膨張 ,  細孔 ,  降伏応力
準シソーラス用語： DSC【熱量測定】 ,  XRD分析 ,  降伏値