小規模機械的試験を使用したHCM12A上の自然形成多層酸化物の機械的特性の評価

Evaluation of the Mechanical Properties of Naturally Grown Multilayered Oxides Formed on HCM12A Using Small Scale Mechanical Testing

著者 (7件)： ABAD M. D. (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA) ,  PARKER S. (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA) ,  FRAZER D. (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA) ,  FIGUEIREDO M. Rebelo (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA) ,  LUPINACCI A. (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA) ,  KIKUCHI K. (Ibaraki Univ., Frontier Res. Center for Applied Nuclear Sci., Mito, JPN) ,  HOSEMANN P. (Univ. of California, Berkeley, Dep. of Nuclear Engineering, Berkeley, CA, USA)
資料名： Oxidation of Metals  (Oxidation of Metals)
巻： 84  号： 1-2  ページ： 211-231  発行年： 2015年08月 
JST資料番号： E0165C  ISSN： 0030-770X  CODEN： OXMEAF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： F/M鋼HCM12Aに液体金属中で成長した多層保護酸化膜の微細構造と機械的完全性を,ラマン分光法,ナノインデンテーション法およびマイクロカンチレバーの試験方法を用いて調査した。ラマンスペクトルはFe₃O₄の外層とCr豊富なスピネル構造の内層を示した。ナノインデンテーション法の結果は,外側層より内側層に対してより高い硬度値を示した。また,内層とバルク鋼との間における拡散層の硬さを測定した。鋼/酸化物界面と酸化物層内の定量的破壊特性を,マイクロカンチレバーテストを利用して測定した。さらに強度及び多層酸化膜の弾性特性を測定した。その結果は,内側のFe-Cr酸化物での多孔質構造が,鋼/酸化物界面の一貫性を制限することを示した。Copyright 2015 Springer Science+Business Media New York Translated from English into Japanese by JST.

シソーラス用語： *高合金鋼 ,  機械的検査 ,  酸化物 ,  *多層構造 ,  *機械的性質 ,  Raman分光分析 ,  ナノインデンテーション ,  片持梁 ,  破壊靱性 ,  微細構造 ,  応力歪曲線
準シソーラス用語： *HCM12A ,  マイクロカンチレバー ,  機械的試験