RE Si Al O N(RE=Y,Lu)ガラスで接合されたSi_3N_4継手の微細構造と性質【Powered by NICT】

Microstructure and Properties of Si_3N_4 Joints Joined with RE-Si-Al-O-N (RE=Y or Lu) Glass

著者 (7件)： Liu Chunfeng (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Wang Xinhua (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Lin Yingkui (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Yu Hongjiang (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Zhang Jie (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Ye Feng (School of Materials Sci. and Engineering, Harbin Inst. of Technol., Harbin) ,  Huang Yudong (School of Chemical Engineering and Technol., Harbin Inst. of Technol., Harbin)
資料名： Guisuanyan Xuebao  (Guisuanyan Xuebao)
巻： 43  号： 3  ページ： 280-285  発行年： 2015年 
JST資料番号： W1454A  ISSN： 0454-5648  CODEN： KSYHA5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： Si_3N_4セラミックは,その場形成されたRE Si Alオキシナイトライドガラス中間層によるSi3N4Al_2O_3RE203SiO2(RE=Y,Lu)粉末混合物を接合した。継手のミクロ組織と特性に及ぼす接合温度,保持時間および希土類元素の種類の影響を調べた。継手の酸化挙動を解析した。保持時間が増加すると層の緻密化と均一性だけでなく,はんだとSi_3N_4マトリックスとしてY-Si-Al-O-Nガラスの間の拡散が改善された。継手は1 550°Cで30分間保持した接合部の接着強さは218MPaであった。さらに,Lu Si Al酸窒化物ガラスを用いるとき,1 200°Cで20h酸化後の継手の強度は室温temperature.で強度の82%である,温度の増加は,シームよりβ-サイアロン相のシームと降水の緻密化を支持することができる。継手の接合強さは接合温度と共に増加した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 接着強さ ,  緻密化 ,  セラミック ,  酸化 ,  保持時間 ,  付着強さ ,  はんだ ,  希土類元素 ,  *継手【接合】 ,  接合部 ,  金属組織
準シソーラス用語： β-SIALON ,  縫目 ,  酸化挙動 ,  接合温度 , 【Automatic Indexing@JST】

分類 (2件)： セラミック・陶磁器一般  (YC03010K) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (8件)： Re ,  Si ,  Al ,  Lu ,  ガラス ,  継手 ,  微細構造 ,  性質