Al-4.6Cu-Mg-0.5Ag合金の微細構造および機械的特性に及ぼすCu/Mg比率および熱処理の影響

Effects of Cu/Mg ratio and heat treatment on microstructures and mechanical properties of Al-4.6Cu-Mg-0.5Ag alloys

著者 (6件)： CHEN Yu-Te (Dep. of Mechanical Engineering, National Central Univ., Jhongli, Taoyuan 320, Taiwan) ,  NIEH Guo-Yu (Materials and Electro-Optics Res. Div., National Chung-Shan Inst. of Sci. and Technol., Lungtang, Taoyuan 325, Taiwan) ,  WANG Jing-Hong (Dep. of Mechanical Engineering, National Central Univ., Jhongli, Taoyuan 320, Taiwan) ,  WU Ten-Fu (Missile and Rocket Systems Res. Div., National Chung-Shan Inst. of Sci. and Technol., Lungtang, Taoyuan 325, Taiwan) ,  LEE Sheng-Long (Inst. of Materials Sci. and Engineering, National Central Univ., Jhongli, Taoyuan 320, Taiwan) ,  LEE Sheng-Long (Dep. of Mechanical Engineering, National Central Univ., Jhongli, Taoyuan 320, Taiwan)
資料名： Materials Chemistry and Physics  (Materials Chemistry and Physics)
巻： 162  ページ： 764-770  発行年： 2015年07月15日 
JST資料番号： E0934A  ISSN： 0254-0584  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Cu/Mg比率の合金を様々なMg元素添加で修飾し,合金をT7およびT8熱処理に懸けた。微細構造変化と対比させて機械的特性を,光学顕微鏡(OM),示差走査熱量測定(DSC),電気導電率計(%IACS)および透過型電子顕微鏡(TEM)で分析した。知見から,Mg量を増加させて合金のCu/Mg比率を下げると,Ωを主要な増強相にする原因となり,溶液や歪硬化の影響を増大させることが分かった。T8熱処理における低温作業手順は,多くの格子欠陥を誘導し,これが,Al-CuおよびMg-Agクラスタの形成を弱めることから,Ω相の圧縮が起きたが,θ’相が強化した。T8状態まで焼き戻されたAl-4.6Cu-Mg-0.5Ag合金の硬度および強度は,加工硬化で増加し,延性を減少させた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *熱処理 ,  処理 ,  低温 ,  アルミニウム合金 ,  *銅含有合金 ,  *マグネシウム含有合金 ,  銀含有合金 ,  *化学組成 ,  *比率 ,  *微細構造 ,  *機械的性質 ,  光学顕微鏡 ,  示差走査熱量測定 ,  電気伝導率 ,  透過型電子顕微鏡 ,  格子欠陥 ,  クラスタ ,  歪硬化 ,  濃度依存性 ,  硬度 ,  強度
準シソーラス用語： 低温処理 ,  導電率

分類 (5件)： 加熱  (PA03040C) ,  無機化合物一般及び元素  (CD01010D) ,  固体の機械的性質一般  (BL01021C) ,  組織的硬化現象  (WB01020C) ,  原子・分子のクラスタ  (BH09030O)

タイトルに関連する用語 (7件)： Al ,  Mg ,  微細構造 ,  機械的特性 ,  Cu ,  比率 ,  熱処理