高比強度で耐食性のマグネシウム合金

A high-specific-strength and corrosion-resistant magnesium alloy

著者 (10件)： XU Wanqiang (Univ. New South Wales, New South Wales, AUS) ,  XU Wanqiang (Australian Res. Council Centre of Excellence for Design in Light Metals, AUS) ,  BIRBILIS Nick (Australian Res. Council Centre of Excellence for Design in Light Metals, AUS) ,  BIRBILIS Nick (Monash Univ., Victoria, AUS) ,  SHA Gang (Nanjing Univ. Sci. and Technol., Jiangsu, CHN) ,  WANG Yu (Univ. New South Wales, New South Wales, AUS) ,  DANIELS John E. (Univ. New South Wales, New South Wales, AUS) ,  XIAO Yang (Zhengzhou Light Metals Res. Inst. Aluminum Corp. China Ltd., Zhengzhou, CHN) ,  FERRY Michael (Univ. New South Wales, New South Wales, AUS) ,  FERRY Michael (Australian Res. Council Centre of Excellence for Design in Light Metals, AUS)
資料名： Nature Materials  (Nature Materials)
巻： 14  号： 12  ページ： 1229-1235  発行年： 2015年12月 
JST資料番号： W1364A  ISSN： 1476-1122  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 超軽量で比強度に優れる構造合金材料であり,冷間加工性は不足するものの,腐食性が高いマグネシウム合金について,超低密度(1.4gcm_-3)の体心立方晶Mg-Li合金の開発によって上述した問題点が解決されることを報告した。特定組成のMg-Li系合金の設計と続いての熱間押出,加熱(溶体化処理)及び水焼入,低温時効処理(<100°C)及び冷間圧延のプロセスによって上記の多機能性特性を発現した。なお,特性の構造的起源はX線回折,透過型電子顕微鏡観察,制限視野電子線回折,原子プローブトモグラフィー及びX線光電子分光法で特性解析した合金はLi過多であり,かつ体心立方母材中の溶質ナノ構造は押出,熱処理及び圧延工程で発現されるものであること,環境に対する耐食性は表面被覆率が旧来の六方最密Mg系合金に比べて非常に大きい均質な炭酸リチウム膜によって生じるものであると思われると結言した。

シソーラス用語： *マグネシウム合金 ,  リチウム含有合金 ,  軽量化 ,  構造材料 ,  比率 ,  焼入 ,  溶体化処理 ,  時効処理 ,  冷間圧延 ,  *耐食性 ,  炭酸リチウム ,  薄膜 ,  延性 ,  X線回折分析 ,  制限視野回折 ,  トモグラフィー ,  被覆率 ,  強度 ,  BCC金属 ,  熱間押出 ,  電子顕微鏡観察 ,  *成形性 ,  ナノ構造 ,  マトリックス【母体】
準シソーラス用語： 原子プローブトモグラフィー ,  透過型電子顕微鏡観察 ,  比強度

分類 (2件)： 機械的性質  (WB02030U) ,  腐食  (WB03030B)

タイトルに関連する用語 (3件)： 比強度 ,  耐食性 ,  マグネシウム合金