O₂+H₂O環境下の600°CでのFeCrAl合金のKCl誘起腐食 予め酸化の影響

KCl-Induced Corrosion of an FeCrAl Alloy at 600 °C in O₂ + H₂O Environment: The Effect of Pre-oxidation

著者 (6件)： ISRAELSSON N. (Chalmers Univ. of Technol., Dep. of Environmental Inorganic Chemistry, High Temperature Corrosion Centre, 412 96 ...) ,  ENGKVIST J. (Chalmers Univ. of Technol., Dep. of Environmental Inorganic Chemistry, High Temperature Corrosion Centre, 412 96 ...) ,  HELLSTROEM K. (Chalmers Univ. of Technol., Dep. of Environmental Inorganic Chemistry, High Temperature Corrosion Centre, 412 96 ...) ,  HALVARSSON M. (Chalmers Univ. of Technol., Dep. of Applied Physics, High Temperature Corrosion Centre, 412 96, Goeteborg, SWE) ,  SVENSSON J.-E. (Chalmers Univ. of Technol., Dep. of Environmental Inorganic Chemistry, High Temperature Corrosion Centre, 412 96 ...) ,  JOHANSSON L.-G. (Chalmers Univ. of Technol., Dep. of Environmental Inorganic Chemistry, High Temperature Corrosion Centre, 412 96 ...)
資料名： Oxidation of Metals  (Oxidation of Metals)
巻： 83  号： 1-2  ページ： 29-53  発行年： 2015年02月 
JST資料番号： E0165C  ISSN： 0030-770X  CODEN： OXMEAF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,600°CでのFeCrAl合金の高温腐食に及ぼすH₂OとKClの影響を調査した。研磨試料をO₂又はO₂+H₂Oに,及びKClを適用したO₂+H₂Oに曝露した。SEM/EDX,XRD,IC,AES及びSIMSにより試料を調査した。KClが腐食を促進し,また急速に成長する鉄リッチ酸化物が時間と共に生成することがわかった。クロム酸塩形成が非保護性酸化物スケールの生成を引き起こすことが明らかになった。暴露前に合金をKClの存在下で予備的に酸化することは,腐食に極めて有益な効果を持つ。Copyright 2014 The Author(s) Translated from English into Japanese by JST.