ナノSiO_2/OTAC共同Pickeringエマルションに基づく水性シリコーンゴムの調製【Powered by NICT】

Preparation of water-based silicone rubber based on nano SiO_2/OTAC collaborative Pickering emulsion

著者 (5件)： Zhai Junling (Lab. of Cellulose and Lignocellulosics Chemistry, Guangzhou Inst. of Chemistry, Chinese Acad. of Sciences, Guangdong ...) ,  Shen Minmin (Lab. of Cellulose and Lignocellulosics Chemistry, Guangzhou Inst. of Chemistry, Chinese Acad. of Sciences, Guangdong ...) ,  Sun Chunning (Lab. of Cellulose and Lignocellulosics Chemistry, Guangzhou Inst. of Chemistry, Chinese Acad. of Sciences, Guangdong ...) ,  Wang Junfeng (Lab. of Cellulose and Lignocellulosics Chemistry, Guangzhou Inst. of Chemistry, Chinese Acad. of Sciences, Guangdong ...) ,  Ha Chengyong (Lab. of Cellulose and Lignocellulosics Chemistry, Guangzhou Inst. of Chemistry, Chinese Acad. of Sciences, Guangdong ...)
資料名： Huagong Xuebao  (Huagong Xuebao)
巻： 66  号： 4  ページ： 1585-1592  発行年： 2015年 
JST資料番号： E0215B  ISSN： 0438-1157  CODEN： HUKHAI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： PickeringエマルションはナノSiO_2と組み合わせたオクタデシルトリメチルアンモニウムクロリド(OTAC)を用いて得られ,線形ポリシロキサン(PDMS)はアルカリ性条件下で開環重合によるD4を合成し,架橋剤KH560はカチオン性水性シリコーンゴム乳濁液を調製するために添加した。Pickering乳濁液SiO_2とOTAC含有量の影響を調べた。SiO_2の表面にOTACの吸収挙動をゼータ電位,TEM及びSEMにより明らかにした。水性シリコーンゴムの構造をFT-IR,~(29)Si NMRスペクトルによって特性化した。ゴム膜の接触角およびショアA硬さに及ぼすKH560の影響も調べた。W(SiO_2)=2.0%の時に乳濁液を最適流動性と安定性を有していた。W(OTAC)=1.75%,OTACの吸収はSiO_2の表面に飽和に達し,単量体転化率は約89%であり,粒径は約617nmであり,ゼータ電位は零に近いとき,PDMSのMnおよびPDIはそれぞれ16036および1.485であった。W(KH560)=5.0%の場合,PDMSはKH560で完全に加水分解し,凝縮した,得られたゴム膜は最適疎水性と硬度を有していた。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *ゴム ,  架橋剤 ,  単量体 ,  *シリコーンゴム ,  加水分解 ,  接触角 ,  疎水性 ,  硬度 ,  乳濁液 ,  キャラクタリゼーション ,  開環重合 ,  ζ電位 ,  ポリジメチルシロキサン
準シソーラス用語： アルカリ性 ,  *Pickeringエマルション , 【Automatic Indexing@JST】

分類 (1件)： 化学工学一般  (XA01000E)

タイトルに関連する用語 (5件)： OTAC ,  共同 ,  Pickeringエマルション ,  シリコーンゴム ,  調製