A novel Ti-6Al-4V alloy microstructure with very high strength and good ductility

著者 (6件)： JIA M.T. (Waikato Centre for Advanced Materials, School of Engineering, The Univ. of Waikato, Hamilton, NZL) ,  ZHANG D.L. (State Key Lab. for Metal Matrix Composites, School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ. ...) ,  ZHANG D.L. (Waikato Centre for Advanced Materials, School of Engineering, The Univ. of Waikato, Hamilton, NZL) ,  GABBITAS B. (Waikato Centre for Advanced Materials, School of Engineering, The Univ. of Waikato, Hamilton, NZL) ,  LIANG J.M. (State Key Lab. for Metal Matrix Composites, School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ. ...) ,  KONG C. (Mark Wainwright Analytical Centre, The Univ. of New South Wales, AUS)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 107  ページ： 10-13  発行年： 2015年10月 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文は,0.52wt.%の比較的高い酸素濃度を持つ粉末成形体鍛造により作製されたTi-6Al-4V(wt.%)合金の溶体化処理,急冷及び時効により形成された,微細な酸素硬化等軸α粒およびナノメーターサイズの針状α相により硬化された微細な変態等軸β粒から成る新たな微細組織について報告する。微細組織は,合金に1352.4MPaの極めて高い引張り降伏強度,1421.7MPaの最大引張強度および7.2%の破断伸びを与えた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： アルミニウム含有合金 ,  バナジウム含有合金 ,  酸素 ,  溶体化処理 ,  *Ti-6Al-4V合金 ,  *延性 ,  機械的強度 ,  酸素含有合金 ,  焼結鍛造 ,  圧粉体 ,  時効処理 ,  α相 ,  β相 ,  等軸組織 ,  焼入 ,  降伏強さ ,  引張強さ ,  伸び
準シソーラス用語： 破断伸び

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (3件)： 延性 ,  Ti-6Al-4V合金 ,  微細組織