プラズマ溶射により製造したナノ構造Fe(AlCr)₂O₄-Cr-(AlCr)₂O₃-Fe複合コーティングの構造と特性

Structure and properties of nanostructured Fe(AlCr)₂O₄-Cr-(AlCr)₂O₃-Fe composite coating prepared by plasma spraying

著者 (5件)： WANG Lei (Key Lab. for New Type of Functional Materials in Hebei Province, Tianjin key laboratory of materials laminating ...) ,  CHEN Xueguang (Key Lab. for New Type of Functional Materials in Hebei Province, Tianjin key laboratory of materials laminating ...) ,  YAN Dianran (Key Lab. for New Type of Functional Materials in Hebei Province, Tianjin key laboratory of materials laminating ...) ,  YANG Yong (Key Lab. for New Type of Functional Materials in Hebei Province, Tianjin key laboratory of materials laminating ...) ,  CHU Zhenhua (Key Lab. for New Type of Functional Materials in Hebei Province, Tianjin key laboratory of materials laminating ...)
資料名： Ceramics International  (Ceramics International)
巻： 41  号： 8  ページ： 9801-9805  発行年： 2015年09月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： その場ナノ構造Fe(AlCr)₂O₄複合コーティング(FACr_52.5コーティング)を,マイクロサイズのAl-Fe₂O₃-Cr₂O₃粉末の反応性プラズマ溶射により製造した。X線回折,走査電子顕微鏡,透過型電子顕微鏡および機械的試験により,微細構造,靱性とビッカース硬さ,及びコーティングの接着強度を調べた。その結果は,FACr_52.5コーティングのラメラ間隔が僅か1μmであることを示した。コーティングはナノ構造の微細構造を示した。その場Cr(20nm)及びFe(50~200nm)粒子はFe(AlCr)₂O₄マトリックス内に均一に分布し,一方,Fe(AlCr)₂O₄マトリックスの結晶粒径は約60nmであった。FACr_52.5複合ナノコーティングは非常に高い硬度を示し,Fe₂O₃-Al粉末を噴霧した複合ナノコーティングのそれと比較してさらに良好な耐摩耗性,強い接着強度と靱性を示した。FACr_52.5コーティングの優れた機械的性質は,コーティングマトリックス中のその場ナノサイズCr粒子の均一な分布に起因した。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： プラズマ溶射 ,  ナノ構造 ,  *クロム ,  *鉄 ,  複合材料 ,  化学合成 ,  微粉体 ,  粒径 ,  靱性 ,  押込硬さ ,  *被覆層 ,  接着強さ ,  層間隔 ,  マトリックス【母体】 ,  *耐摩耗性 ,  均一性 ,  分散粒子 ,  *鉄酸塩 ,  アルミニウム化合物 ,  クロム化合物 ,  セラミック被覆
準シソーラス用語： その場合成

分類 (1件)： 金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (5件)： プラズマ溶射 ,  ナノ構造 ,  Fe ,  Cr ,  コーティング