セルロースナノファイバで強化したバイオベースポリウレタン:界面の効果に関する包括的調査

Bio-based polyurethane reinforced with cellulose nanofibers: A comprehensive investigation on the effect of interface

著者 (8件)： BENHAMOU Karima (Fac. of Sciences and Technologies, Lab. of Organometallic and Macromolecular Chemistry-Composite Materials, Cadi ...) ,  BENHAMOU Karima (Univ. Grenoble Alpes, LGP2, F-38000 Grenoble, FRA) ,  BENHAMOU Karima (CNRS, LGP2, F-38000 Grenoble, FRA) ,  KADDAMI Hamid (Fac. of Sciences and Technologies, Lab. of Organometallic and Macromolecular Chemistry-Composite Materials, Cadi ...) ,  MAGNIN Albert (Lab. Rheologie et Procedes, Grenoble-INP, UJF Grenoble 1, UMR CNRS 5520, B.P. 53, 38041 Grenoble Cedex 9, FRA) ,  DUFRESNE Alain (Univ. Grenoble Alpes, LGP2, F-38000 Grenoble, FRA) ,  DUFRESNE Alain (CNRS, LGP2, F-38000 Grenoble, FRA) ,  AHMAD Azizan (School of Chemical Sciences and Food Technol., Fac. of Sci. and Technol., Universiti Kebangsaan Malaysia, 43600 ...)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 122  ページ： 202-211  発行年： 2015年05月20日 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ナツメヤシの木の穂軸から抽出したセルロースナノファイバとポリカプロラクトン(PCL)ジオール基盤ポリウレタン(PU)とからなるバイオベースポリウレタンナノ複合体をキャスティング/蒸発により調製した。2タイプのナノファイバ,セルロースナノフィブリル(CNF)およびセルロースナノ結晶(CNC)を用いた。ナノ複合体の機械的および熱的性質をDMA,DSC,および引っ張り試験で検討し,モルホロジーをSEMにより調べた。バイオナノ複合体はニートPUよりも優れた機械的性質を示した。両ナノフィラーを比較すると機械的および熱的性質の改善はCNF基盤ナノ複合体の方がより顕著であり,それはCNFの高いアスペクト比のみならずPUマトリックス中での良好な分散により説明することができた。ナノフィラー界面重合体およびPUセグメントの溶解度パラメータの計算はCNCに比べてCNF基盤ナノ複合体の方が優れた界面接着の前兆になる。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 植物繊維 ,  ナノファイバ ,  生分解性高分子 ,  *ポリウレタン ,  接着 ,  ナノ複合材料 ,  ナノ構造 ,  繊維 ,  ナノ結晶 ,  *バイオベースポリマ
準シソーラス用語： ナノフィブリル ,  *ナノ複合体 ,  *界面接着

分類 (2件)： 多糖類  (CF10054P) ,  ポリウレタン  (YH07130G)

タイトルに関連する用語 (4件)： セルロースナノファイバ ,  強化 ,  界面 ,  調査