加圧ガス処理による純鉄中の窒化速度の大幅な加速

Significant acceleration of nitriding kinetics in pure iron by pressurized gas treatment

著者 (7件)： WANG Bo (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  FU Wantang (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  DONG Fan (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  JIN Guofeng (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  FENG Weiwei (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  WANG Zhenhua (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  SUN Shuhua (State Key Lab. of Metastable Materials Sci. and Technol., Coll. of Materials Sci. and Engineering, Yanshan Univ. ...)
資料名： Materials & Design  (Materials & Design)
巻： 85  ページ： 91-96  発行年： 2015年11月15日 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 500°Cで5時間の加圧ガス窒化を行う事によって,純鉄中の窒化物生成および窒化速度に及ぼす窒化圧力の効果を調べた。窒化ガス圧を1気圧(従来の窒化条件)から5気圧に増やす事によって,窒化層厚みが約210μmから1100μmに大幅に増加した。更に,化合物層の組成を窒化圧力変化により制御出来る事が明らかになった。これらの改善は,加圧ガス窒化処理中の窒素の高速反応速度および高度な内側拡散流束による。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 加圧 ,  *純鉄 ,  加速 ,  *ガス窒化 ,  表面改質 ,  窒化物 ,  窒化層 ,  層厚 ,  拡散 ,  硬度 ,  鉄化合物 ,  ε相 ,  γプライム相 ,  圧力効果 ,  表面性状 ,  アンモニア ,  *反応速度 ,  高圧気体 ,  フラックス【流束】 ,  化学ポテンシャル ,  金属板
準シソーラス用語： *加圧ガス窒化 ,  拡散流束 ,  窒化鉄 ,  表面硬さ

分類 (1件)： 表面硬化熱処理  (WC03030E)

タイトルに関連する用語 (4件)： 加圧ガス ,  純鉄 ,  窒化 ,  加速