純銅の微細組織と微小硬さに及ぼす低温衝撃変形とその後の焼なましの影響

Effect of cryogenic impact deformation and subsequent annealing on microstructure and microhardness of pure copper

著者 (5件)： LUO Wei (State Key Lab. of Silicon Materials, Key Lab. of Novel Materials for Information Technol. of Zhejiang Province ...) ,  GONG Hailong (State Key Lab. of Silicon Materials, Key Lab. of Novel Materials for Information Technol. of Zhejiang Province ...) ,  WANG Qiming (Quality Inspection Dep., Hangzhou Hangyang Co. Ltd., 99 Donghuan Road, Zhejiang Linan Economic Dev. Zone, Hangzhou ...) ,  LU Jiangxu (State Key Lab. of Silicon Materials, Key Lab. of Novel Materials for Information Technol. of Zhejiang Province ...) ,  YAN Mi (State Key Lab. of Silicon Materials, Key Lab. of Novel Materials for Information Technol. of Zhejiang Province ...)
資料名： Materials Letters  (Materials Letters)
巻： 157  ページ： 315-317  発行年： 2015年10月15日 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本記事は粗粒銅において有効な結晶粒微細化に低温衝撃変形を応用することについて発表している。超微粒化細微細視組織を,7.35ms^-1の初期衝撃速度を持つエアーハンマーを用いて低温衝撃変形により処理した。歪ε=2.21に対してTEM観察は,初期の等軸粗粒(18μm)が低角粒界により輪郭を描いたサブミクロン寸法の狭いドメインのラメラ組織に発達することを示した。変形した試料の微小硬さは,74.2±1.2HVから118.3±1.8HVに増加した。その後,190°Cで60分間焼なますと,転位密度の著しい減少をもたらした。残留しているナノ寸法の双晶で埋込まれた(175nmの平均幅を持つ)伸びた超微細粒を焼なました試料で観測した。本研究は,バルクの超微細粒材料を作り出すための低温衝撃変形の可能性に光を当てている。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 純金属 ,  *銅 ,  *変形組織 ,  *微小硬さ ,  変形 ,  *焼なまし ,  *結晶粒微細化 ,  超微粒子 ,  歪 ,  結晶粒界 ,  層状組織 ,  転位密度 ,  衝撃 ,  低温 ,  小傾角粒界 ,  材料
準シソーラス用語： *純銅 ,  *衝撃変形 ,  *超微細粒材料