FeNiCoAlNbB合金のミクロ組織と機械的性質に及ぼす時効時間の影響【Powered by NICT】

Influence of aging time on microstructure and mechanical properties of FeNiCoAlNbB alloy

著者 (7件)： Qu Guili (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Peng Wenyi (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Chen Zhaoxia (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Yang Nengwu (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Yan Mingming (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Wang Weiwei (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang) ,  Shi Haiping (School of Materials Sci. and Engineering,Nanchang Univ., Jiangxi, Nanchang)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 40  号： 3  ページ： 109-114  発行年： 2015年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 研究対象としてFe(39.35)Ni(30)Co(18)Al(10.5Nb_2B(0.15)形状記憶合金に基づいて,合金のミクロ組織と機械的性質に及ぼす時効時間の影響をX線回折,SEM,圧力試験機,金属顕微鏡とエネルギー分散分光法により調べた。結果は,加齢に伴う時間の増加,γ’相とB2相は連続的に析出し,γ′相の析出はオーステナイト母相を強化し,B2相の析出は合金の延性を低下させることを示した。擬弾性曲線は873~Kで,加齢に伴う時間の増加,圧縮強度,回復可能な歪と合金の硬さは最初増加し,それから減少することを示した。しかし,合金の最大歪は,最初に急速に増加し,その後ゆっくり増加した。時効時間が60hの場合,圧縮強度,回復可能な変形と合金の硬さは全ての最大に達し,1239.05MPa,10.76%と496HV10であった。しかし合金の残留歪は相対的に最小であった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 残留歪 ,  オーステナイト ,  *合金 ,  圧縮強さ ,  *機械的性質 ,  硬度 ,  加齢 ,  *時効 ,  延性 ,  γプライム相 ,  形状記憶合金 ,  擬弾性 ,  金属顕微鏡 ,  *金属組織