充填PIBベース感圧接着剤のレオロジーと接着特性。I レオロジーと剪断抵抗

Rheology and adhesive properties of filled PIB-based pressure-sensitive adhesives. I. Rheology and shear resistance

著者 (6件)： KOSTYUK Anna (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS) ,  IGNATENKO Viktoria (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS) ,  SMIRNOVA Nina (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS) ,  BRANTSEVA Tatiana (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS) ,  ILYIN Sergey (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS) ,  ANTONOV Sergey (A.V. Topchiev Inst. of Petrochemical Synthesis, Russian Acad. of Sci., Moscow, RUS)
資料名： Journal of Adhesion Science and Technology  (Journal of Adhesion Science and Technology)
巻： 29  号： 17/20  ページ： 1831-1848  発行年： 2015年09月 
JST資料番号： T0475A  ISSN： 0169-4243  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ポリイソブチレン(PIB)に,ナノシリカ(NS)(5~20wt%),またはハロイサイトナノチューブ(HNT)(5~40wt%)を添加し,レオロジー特性とステンレス鋼板の剪断抵抗(1kg荷重下での剥離までの時間)を測定した。その結果,HNT系は流動曲線に降伏点を示し,フィラーのネットワークが形成されていることを示した。その降伏応力は含量に連れて増加した。NS系では降伏点はなく,含量に連れて粘度は増加し,ずり増粘を示した。剪断抵抗は,NS系は20wt%で,2桁以上も増大した。一方,HNT系は40wt%でも8倍以下であった。この剪断抵抗とレオロジーデータを結びつけるモデルを構築し,予測結果と実験値を比較し,議論した。

シソーラス用語： *ポリイソブチレン ,  *感圧接着剤 ,  レオロジー ,  特性 ,  ナノ粒子 ,  *ハロイサイト ,  *ナノチューブ ,  ずり粘度 ,  抵抗 ,  接着強さ ,  クリープ
準シソーラス用語： ずり増粘 ,  *ナノシリカ ,  *レオロジー特性 ,  *剪断抵抗 ,  コールドフロー