高温水中の合金690の溶接熱影響部と応力腐食割れにおける微細構造,局所変形,微量化学の特性化

Characterization of microstructure, local deformation and microchemistry in Alloy 690 heat-affected zone and stress corrosion cracking in high temperature water

著者 (6件)： LU Zhanpeng (Inst. of Materials Sci., School of Materials Sci. and Engineering, Shanghai Univ., Shanghai 200072, CHN) ,  LU Zhanpeng (State Key Lab. of Advanced Special Steels, Shanghai Univ., Shanghai 200072, CHN) ,  CHEN Junjie (Inst. of Materials Sci., School of Materials Sci. and Engineering, Shanghai Univ., Shanghai 200072, CHN) ,  SHOJI Tetsuo (New Ind. Creation Hatchery Center, Tohoku Univ., Sendai 980-8579, JPN) ,  TAKEDA Yoichi (New Ind. Creation Hatchery Center, Tohoku Univ., Sendai 980-8579, JPN) ,  YAMAZAKI Seiya (New Ind. Creation Hatchery Center, Tohoku Univ., Sendai 980-8579, JPN)
資料名： Journal of Nuclear Materials  (Journal of Nuclear Materials)
巻： 465  ページ： 471-481  発行年： 2015年10月 
JST資料番号： D0148A  ISSN： 0022-3115  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 合金690の溶接熱影響部における溶融線からの距離が増すと,マイクロ硬度が低下し,核平均配向不整が低下し,Σ3境界比率が増大する。合金690の溶接熱影響部の結晶粒界におけるクロム欠乏は合金600熱影響部におけるそれよりも有意に少ない。模擬PWR型原子炉一次水中の合金690熱影響部は合金600熱影響部よりも遥かに高い粒界応力腐食割れ抵抗を示す。強冷間加工合金690は局所粒界応力腐食割れを示す。冶金学的性質と機械的性質が合金690の応力腐食割れに及ぼす影響を論じた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *インコネル ,  *応力腐食割れ ,  微細構造 ,  変形 ,  微量分析 ,  *溶接熱影響部 ,  熱影響 ,  PWR型原子炉 ,  原子炉用鋼 ,  結晶粒界 ,  局所変形 ,  微量化学 ,  *Alloy690 ,  *亀裂 ,  *腐食割れ
準シソーラス用語： *合金690 ,  熱影響部

分類 (1件)： 原子炉の構成要素と原子炉材料一般  (MD04010I)

タイトルに関連する用語 (8件)： 高温水 ,  合金690 ,  溶接熱影響部 ,  応力腐食割れ ,  微細構造 ,  局所変形 ,  微量化学 ,  特性化