冷噴霧沈着を使用するナノダイヤモンド強化アルミニウム金属母材複合材の合成

Synthesis of nanodiamond-reinforced aluminum metal matrix composites using cold-spray deposition

著者 (6件)： WOO D.J. (Dep. of Physics, Naval Postgraduate School, 833 Dyer Road, Monterey, CA 93943, USA) ,  HEER F.C. (Dep. of Mechanical and Aerospace Engineering, Naval Postgraduate School, 700 Dyer Road, Monterey, CA 93943, USA) ,  BREWER L.N. (Dep. of Mechanical and Aerospace Engineering, Naval Postgraduate School, 700 Dyer Road, Monterey, CA 93943, USA) ,  HOOPER J.P. (Dep. of Physics, Naval Postgraduate School, 833 Dyer Road, Monterey, CA 93943, USA) ,  OSSWALD S. (Dep. of Physics, Naval Postgraduate School, 833 Dyer Road, Monterey, CA 93943, USA) ,  OSSWALD S. (Dep. of Mechanical and Aerospace Engineering, Naval Postgraduate School, 700 Dyer Road, Monterey, CA 93943, USA)
資料名： Carbon  (Carbon)
巻： 86  ページ： 15-25  発行年： 2015年05月 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 10wt%のNDを含むボールミル粉砕粉末の低圧の冷噴霧(CS)沈着によって,緻密なナノダイヤモンド-アルミニウム(ND-Al)の複合材被覆を首尾よく生産した。高エネルギーボールミル粉砕は,ND塊の粒径分布や結晶サイズ,分散に優れた制御性を提供するので,複合材供給原料粉末の合成の実用的手段である。得られたCS被覆を沈着効率や粒子速度と機械的性質に関して特性化した。CS沈着は供給原料粉末に比べて高い硬度と弾性率の両方を有する緻密なND-Al複合材被覆を生産できることがわかった。最高の沈着効率(14.2%)を持つ0.5h粉砕ND-Al複合材の被覆硬度は3.02GPaであり,無処理Al(1.10GPa)より175%の増加である。複合材被覆の最高の弾性率が98.3GPaであり,Al粉末を51.5%上回る。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ナノ複合材料 ,  ナノ結晶 ,  *ダイヤモンド ,  *アルミニウム ,  微粉砕 ,  噴霧法 ,  被覆 ,  ステンレス鋼 ,  プロセスパラメータ ,  表面性状 ,  硬度 ,  弾性係数