重合性イオン性液体共重合体P(MMA Co BVIm Br)とPVDFブレンド膜の表面濡れ性に及ぼすその影響【Powered by NICT】

Polymerizable Ionic Liquid Copolymer P(MMA-co-BVIm-Br) and Its Effect on the Surface Wettability of PVDF Blend Membranes

著者 (6件)： Du Chunhui (School of Environmental Sci. and Engineering, Zhejiang Gongshang Univ., Hangzhou) ,  Ma Xumin (School of Environmental Sci. and Engineering, Zhejiang Gongshang Univ., Hangzhou) ,  Wu Chunjin (School of Environmental Sci. and Engineering, Zhejiang Gongshang Univ., Hangzhou) ,  Cai Meiqiang (School of Environmental Sci. and Engineering, Zhejiang Gongshang Univ., Hangzhou) ,  Hu Mengxin (Schoolof Food Sci. and Biotechnology, Zhejiang Gongshang Univ., Hangzhou) ,  Wang Ting (School of Environmental Sci. and Engineering, Zhejiang Gongshang Univ., Hangzhou)
資料名： Chinese Journal of Polymer Science  (Chinese Journal of Polymer Science)
巻： 33  号： 6  ページ： 857-868  発行年： 2015年 
JST資料番号： C2566A  ISSN： 0256-7679  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： シンガポール (SGP)  言語： 英語 (EN)

抄録/ポイント： 重合性イオン液体共重合体P(MMA Co BVIm Br)をラジカル重合法により合成し,Fourier変換赤外分光法(FTIR),~1H核磁気共鳴(~1H-NMR)およびゲル浸透クロマトグラフィー(GPC)によって特性化した。得られた共重合体を用いて,相反転法によりポリ(フッ化ビニリデン)(PVDF)ブレンド膜を調製した。ブレンド膜の多形,表面湿潤性とゼータ電位(ζ)に及ぼす共重合体の影響をATR-FTIR,接触角装置およびゼータ電位分析器で調べた。走査型電子顕微鏡(SEMとSEM-EDS)も形態と製作した膜の表面要素変化を調べるために適用した。結果はP(MMA Co BVIm Br)共重合体は,ブレンド膜は,実験pH範囲で正の表面を持つとした膜の表面に存在することを示した。共重合体は,PVDF膜におけるβ結晶相の形成に有利であった。接触角実験はP(MMA Co BVIm Br)共重合体は,Br~-アニオンを交換PF_6~-によるブレンド膜の濡れ性を親水性から疎水性にできることを示した。純PVDF膜と比較して,ブレンド膜の水フラックスと水回収フラックスは明らかに増加した。フラックス回収率(FR)と全ファウリング比(R_t)からの結果は,全てのブレンド膜は優れた耐ファウリング特性を有することを示唆した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *濡れ ,  溶接フラックス ,  接触角 ,  吸湿性 ,  キャラクタリゼーション ,  ζ電位 ,  FTIR分光法 ,  *共重合体 ,  *ポリフッ化ビニリデン
準シソーラス用語： ファウリング ,  水フラックス ,  PVDF膜 ,  ATR-FTIR分光法 ,  転相 ,  *表面濡れ性 , 【Automatic Indexing@JST】