エネルギー貯蔵熱調整PA6/CPCM繊維の調製とキャラクタリゼーション【Powered by NICT】

Preparation and characterization of energy-storage thermo-regulated PA6/CPCM fiber

著者 (5件)： Wu Chao (State Key Lab. for Chemical Fibers Modification and Polymer Materials,Coll. of Material Sci. and Engineering,Donghua ...) ,  Zou Liming (State Key Lab. for Chemical Fibers Modification and Polymer Materials,Coll. of Material Sci. and Engineering,Donghua ...) ,  Zhang Shengkai (State Key Lab. for Chemical Fibers Modification and Polymer Materials,Coll. of Material Sci. and Engineering,Donghua ...) ,  Ni Jianhua (State Key Lab. for Chemical Fibers Modification and Polymer Materials,Coll. of Material Sci. and Engineering,Donghua ...) ,  Shao Qiliang (State Key Lab. for Chemical Fibers Modification and Polymer Materials,Coll. of Material Sci. and Engineering,Donghua ...)
資料名： Hecheng Xianwei Gongye  (Hecheng Xianwei Gongye)
巻： 38  号： 2  ページ： 15-18  発行年： 2015年 
JST資料番号： C2123A  ISSN： 1001-0041  CODEN： HXIGEU  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ,二種類の固体-液体相変化材料の混合物,コアとPA6としてシースとして,CPCMとエネルギー貯蔵温度調節ポリアミド6/composite相変化材料(PA6/CPCM)紡糸したままの繊維は,非伝統的溶融紡糸プロセスを介して自作複合紡糸パックを用いて調製した。紡糸したままの繊維は80°Cで5倍に延伸エネルギー貯蔵温度調節PA6/CPCM繊維を製造した。繊維の構造と性質を特性化した。結果はPA6/CPCM紡糸したままの繊維は直径約95μmの芯鞘構造を有していることを示した。得られた繊維はCPCMの質量分率を有していた約32 9%,融解相変化温度1850 - 30 89°C,結晶化相変化温度778 - 18 68°C,融解エンタルピー66 12,結晶化エンタルピー64 93J/g;エネルギー貯蔵温度調節PA6/CPCM繊維は8mL/hとしてCPCMの注入速度として15 57dtex,破断強度2 76cN/dtex,破断時の伸び16 71%の線密度を持っていた;この繊維は熱コートに適用した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 温度制御 ,  結晶化 ,  *エネルギー貯蔵 ,  紡糸 ,  *ナイロン6 ,  破断 ,  融解 ,  エンタルピー ,  *キャラクタリゼーション ,  相転移 ,  溶融紡糸
準シソーラス用語： 線密度 ,  質量分率 ,  複合紡糸 ,  相変化材料 , 【Automatic Indexing@JST】