準安定βTi-V合金の相安定性への応力誘起オメガ遷移と機械的双晶化の依存関係

Dependence of stress-induced omega transition and mechanical twinning on phase stability in metastable β Ti-V alloys

著者 (5件)： WANG X.L. (Shanghai Key Lab. of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong Univ., Shanghai ...) ,  LI L. (Shanghai Key Lab. of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong Univ., Shanghai ...) ,  MEI W. (Shanghai Key Lab. of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong Univ., Shanghai ...) ,  WANG W.L. (Shanghai Key Lab. of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong Univ., Shanghai ...) ,  SUN J. (Shanghai Key Lab. of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong Univ., Shanghai ...)
資料名： Materials Characterization  (Materials Characterization)
巻： 107  ページ： 149-155  発行年： 2015年09月 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 一連の二元βTi-16~22V合金の引張特性と変形ミクロ組織を調べた。結果は,βTi-16~22wt.%V合金のバナジウム含有量の増加により,塑性変形モードが,{-5052}_ω∥{3-3-2}_βの特別な晶癖面を持つプレート状応力誘起ω相変態から,{332}<113>タイプの変形双晶化へ変化することを示した。プレート状応力誘起ω相は,β相マトリックスと特別な方位関係,すなわち,[110]_β∥[-12-10]_ω,(3-3-2)_β∥(-5052)_ωと(-55-4)_β∥(30-31_ω)を持っていた。相変態への応力誘起により塑性的に変形した合金は,{332}<113>タイプの変形双晶化により変形したものより比較的高い降伏強度を示した。β相の安定性は,塑性変形モードで重要な役割を果たす,すなわち,応力誘起ω相変態あるいは{332}<113>タイプ変形双晶化は,βTi-16~22wt.%V合金の機械的性質を支配すると結論できた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *相安定性 ,  *チタン合金 ,  二元合金 ,  塑性変形 ,  変形双晶 ,  バナジウム含有合金 ,  準安定相 ,  β相 ,  改変 ,  変形組織 ,  加工誘起変態 ,  晶癖 ,  界面 ,  降伏強さ ,  *ω相
準シソーラス用語： 引張特性 ,  *双晶化

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (8件)： Ti ,  V合金 ,  相安定性 ,  応力 ,  誘起 ,  オメガ ,  遷移 ,  依存関係