ポリフェニレンスルフィドの摩擦及び摩耗特性に及ぼす固相の結晶構造と熱処理の影響【Powered by NICT】

Effect of Crystal Structure and Heat Treatment in Solid Phase on the Frictional and Wear Properties of Polyphenylene Sulfide

著者 (6件)： Luo Wei (State Key Lab. of Polymer Materials Engineering, Polymer Res. Inst. of SichuanUniversity, Chengdu) ,  Li Maoyuan (Beijing Overall-Design Dep. of Electromechanical Engineering, Beijing) ,  Ge Yaning (Sichuan Changhong Mould Technol. Co., Ltd., Mianyang) ,  Hong Yiqiang (Beijing Overall-Design Dep. of Electromechanical Engineering, Beijing) ,  Zou Huawei (State Key Lab. of Polymer Materials Engineering, Polymer Res. Inst. of SichuanUniversity, Chengdu) ,  Liang Mei (State Key Lab. of Polymer Materials Engineering, Polymer Res. Inst. of SichuanUniversity, Chengdu)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 31  号： 3  ページ： 37-41  発行年： 2015年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なった結晶性を有するポリフェニレンスルフィド(PPS)試料を固相中での熱処理の温度と時間を制御することにより調製した。またPPS試料の摩擦と摩耗特性を,リング・オン・ブロック摩擦試験機により調べた。sampleswasの結晶化挙動示差走査熱量測定(DSC)と広角X線回折(XRD)により検討した。結果は結晶度と結晶構造はPPSの摩擦と摩耗特性に及ぼす顕著な効果を持つことを示した。120°C2時間で処理したPPS試料の結晶性は,未処理のものよりも118%高かった。また摩耗速度は96.8%減少し,摩擦は0.58~0.45coefficientreduces。高温(270 °C)で加熱したPPSの主な摩耗機構は,アブレシブ及び疲れ摩耗である。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *結晶構造 ,  *摩耗 ,  示差走査熱量測定 ,  *ポリフェニレンスルフィド ,  摩耗速度 ,  *熱処理 ,  *摩耗特性 ,  高温 ,  結晶度 ,  X線回折 ,  *固相 ,  摩擦試験
準シソーラス用語： 摩耗機構 ,  広角X線回折 ,  結晶化挙動 , 【Automatic Indexing@JST】