高速ドライエンドミル用のCrTiAlN被膜のミクロ組織とカッティング性能

Microstructure and cutting performance of CrTiAlN coating for high-speed dry milling

著者 (8件)： Lu Li (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Wang Qimin (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Chen Bingzhou (Kunshan Kedun Nano Coatings Tech. Co. Ltd., Suzhou) ,  Ao Yongcui (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Yu Donghai (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Wang Chengyong (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Wu Shanghua (School of Electromechanical Engineering, Guangdong Univ. of Technol., Guangzhou) ,  Kim Kwang Ho (National Core Res. Center for Hybrid Materials Solution, Pusan National Univ., Korea, Busan)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 24  号： 6  ページ： 1800-1806  発行年： 2014年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 閉鎖磁界不均衡マグネトロンスパッタリング装置を使って超硬合金製エンドミルにCrTiAlN硬質皮膜を被覆した。それは,Crの接着層,CrNの中間層,およびCrTiAlNの最上層から成った。X線回折(XRD),走査電子顕微鏡(SEM)観察,透過電子顕微鏡(TEM)観察,微小押込試験,およびスクラッチ試験を実施して,本被膜のミクロ組織と機械的性質を研究した。高速ドライエンドミル用焼入鋼(P20,HRC45)を使って表面被覆エンドミルのカッティング性能試験を実施した。試験結果から,本被膜はナノ層の(Cr,Ti,Al)Nの柱状晶であった。本被膜は,超硬合金基板に対する良い接着性と約30GPaの高い微小硬さを示した。表面被覆エンドミルは非被覆のものと比較して,工具寿命の大幅な向上と非常に低い切削抵抗を示した。その関連機構を考察した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 切削性 ,  *金属組織 ,  チタン化合物 ,  アルミニウム化合物 ,  エンドミル ,  皮膜 ,  マグネトロンスパッタリング ,  スパッタリング装置 ,  透過型電子顕微鏡 ,  引かき試験 ,  走査電子顕微鏡 ,  機械的性質 ,  性能試験 ,  X線回折 ,  微小硬さ ,  切削抵抗 ,  超硬合金 ,  工具寿命
準シソーラス用語： カッティング性能 ,  スクラッチ試験 ,  *ミクロ組織【金属組織】 ,  硬質皮膜 ,  透過電子顕微鏡