レーザアブレーション法で作製したナノ粉末を用いた透明YbドープLu₂O₃セラミックスの焼結

Sintering of transparent Yb-doped Lu₂O₃ ceramics using nanopowder produced by laser ablation method

著者 (6件)： KIJKO V.S. (Ural Federal Univ. named after the first President of Russia B.N. Yeltsin, Mira St. 19, Ekaterinburg 620002, RUS) ,  MAKSIMOV R.N. (Ural Federal Univ. named after the first President of Russia B.N. Yeltsin, Mira St. 19, Ekaterinburg 620002, RUS) ,  MAKSIMOV R.N. (Inst. of Electrophysics UB RAS, Amundsen St.106, Ekaterinburg 620016, RUS) ,  SHITOV V.A. (Inst. of Electrophysics UB RAS, Amundsen St.106, Ekaterinburg 620016, RUS) ,  DEMAKOV S.L. (Ural Federal Univ. named after the first President of Russia B.N. Yeltsin, Mira St. 19, Ekaterinburg 620002, RUS) ,  YUROVSKIKH A.S. (Ural Federal Univ. named after the first President of Russia B.N. Yeltsin, Mira St. 19, Ekaterinburg 620002, RUS)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 643  ページ： 207-211  発行年： 2015年09月15日 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 通常の真空および放電プラズマ焼結によって透明YbドープLu₂O₃セラミックスを作製した。出発材料として,レーザアブレーションで合成したナノ粒子を用いた。ナノ粉末の形態と相の進展について,透過型電子顕微鏡と同時の熱分析とX線回折により調べた。得られたナノ粒子は単斜晶相であったが,1100°Cで1時間のか焼をした後では立方晶に完全に置き換わっていた。Yb:Lu₂O₃粉末圧縮体を1780°Cで20時間の通常の真空焼結を行なった結果,平均結晶粒径が1.6μmで1080nmでの光透過率が79.3%の完全高密度セラミックスが得られた。15kNの圧力下,1450°Cで40分間か焼したYb:Lu₂O₃ナノ粒子を放電プラズマ焼結すると,粒径が0.2μmで1080nmでの光透過率が75.6%のセラミックスが得られた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *酸化ルテチウム ,  イッテルビウム ,  ドーピング ,  機能性セラミック ,  *透明材料 ,  *放電プラズマ焼結 ,  真空処理 ,  レーザアブレーション ,  ナノ構造 ,  微粉体 ,  か焼 ,  単斜晶系 ,  立方晶系 ,  結晶粒度 ,  透過率 ,  光透過 ,  緻密化 ,  密度
準シソーラス用語： ナノ粉末 ,  光透過率 ,  高密度化 ,  真空焼結

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (8件)： レーザアブレーション法 ,  作製 ,  ナノ粉末 ,  Yb ,  ドープ ,  Lu2O3 ,  セラミックス ,  焼結